Morphological Characterization of Combustion Deposited Diamond Crystals and Films
نویسندگان
چکیده مقاله:
Single crystals and polycrystalline diamond films of several thicknesses were deposited using oxygen/acetylene combustion flame technique. The substrate used was pure polycrystalline molybdenum subjected to mechanical polishing. Quality and microstructural characteristic of diamond produced were investigated using X-Ray diffraction, Raman Spectroscopy, Scanning and Transmission Electron Microscopy. Results obtained revealed that a good quality single and polycrystalline diamond could be produced. However, a combination of various defects such as twins, dislocations and stacking faults are always present.
منابع مشابه
Morphological, structural and photoresponse characterization of ZnO nanostructure films deposited on plasma etched silicon substrates
ZnO nanostructure films were deposited by radio frequency (RF) magnetron sputtering on etched silicon (100) substrates using dry Ar/SF6 plasma, at two etching times of 5 min and 30 min, and on non etched silicon surface. Energy dispersive X-ray (EDX) technique was employed to investigate the elements contents for etched substrates as well as ZnO films, where it is found to be stoichiometric. Su...
متن کاملPiezoresistivity in vapor-deposited diamond films
We report the observation of a very large piezoresistive effect in both polycrystalline and homoepitaxial chemical-vapor-deposited diamond films. The gauge factor for polycrystalline p-type diamond at 500 microstrains was found to be only 6 at room ambient, but increased rapidly with temperature, exceeding that of polycrystalline silicon (30) at 35 ‘C, and that of single-crystal Si (120) at 50 ...
متن کاملCharacterization of diamond-like carbon films deposited on commercially pure Ti and Ti–6Al–4V
The diamond-like carbon (DLC) films deposited on the articulating surface of medical-grade Ti and Ti–6Al–4V were characterized. The DLC films were synthesized by r.f. plasma assisted chemical vapor deposition (PACVD) using C6H6 at 10 mTorr. For wear tests, the ball-ondisk type wear tester was employed by wearing a 5-mm diameter ruby ball against a rotating metal disk. The DLC coating dramatical...
متن کاملDiamond films from combustion of methyl acetylene and propadiene
To date diamond films grown with the combustion technique have used either acetylene or, rarely, ethylene as the fuel. However, there are barriers to large scale commercialization of the combustion technique using either fuel. For example, acetylene is relatively expensive and difficult to handle, while the use of ethylene gives relatively low growth rates. In this letter we propose replacing a...
متن کاملSurface stabilization phenomena on flame-deposited diamond single crystals
The acetylene-oxygen combustion flame technique was applied to the homoepitaxial deposition of diamond single crystals on cylindrically shaped {111}, {001} and {110} type IIa natural diamond substrates. After deposition the specimen revealed surface stabilization phenomena like flat facets and curved bands for orientations corresponding to Miller indices {hhk}h < k in the (110) zones. The surfa...
متن کاملOrientation dependent surface stabilization on flame deposited diamond single crystals
In this study a model for the orientation dependent surface stabilization of diamond grown from the vapour phase is presented. The model is based on a first order broken bond analysis of the diamond crystal with additional considerations about surface reconstruction by dimer formation. Due to the formation of dimers, surface stabilization is expected for orientations corresponding to Miller ind...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 15 شماره 3
صفحات 255- 260
تاریخ انتشار 2002-10-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023