Moisture Diffusion Properties of Fabric Composite (Glass Fiber/Epoxy Resin)
نویسنده
چکیده مقاله:
In this study, the effect of hygrothermal conditioning on the moisture diffusion properties of the fabric composite (glass fiber/epoxy resin) was investigated. The water uptake of the specimens conditioned in humid environment at different relative humidities (0, 60 and 96 % r.h) at constant temperature (60°C) was evaluated by weight gain measurements. The moisture diffusion properties of the fabric composite (glass fiber/epoxy resin) were determined using standard weight gain method. The weight gain experiments were performed to determine the equilibrium moisture content Mm of the fabric composite as a function of relative humidity (r.h). The measured weight gain is then fit to the solution to the diffusion equation (Fick’s law) to determine the diffusivity D. The comparison carried out between the values obtained of the characteristic parameters (D and Mm) of the kinetics of water absorption by the hygrothermal test of conditioning carried out into the laboratory and those given by Loos and Springer confirms the following principal remarks clearly: the diffusion coefficient D and the maximum weight gain Mm depend not only on the nature of material but also of the environmental conditions (hygrothermal conditioning). The maximum concentration of water (matrix+interface) obtained from calculations based on measured values, where a homogeneous diffusion phenomenon is assumed inside the material (Df=0), shows clearly that the presence of fibers in a polymeric matrix reduces the water up-take of the matrix by about 4 times.
منابع مشابه
Microleakage Evaluation of Class II Composite Resin Restorations with Different Thicknesses of Resin-Modified Glass Ionomer
Background and Aim: One of the weaknesses of Class II composite resin restorations is gingival microleakage which contributes to postoperative sensitivity and secondary caries. The aim was to evaluate the microleakage in Class II composite resin restorations with different thicknesses of resin-modified glass ionomer (RMGI). Materials and Methods: In this in-vitro study, standardized Class II s...
متن کاملMoisture Diffusion Analysis of Composite Strength Degradation
Moisture diffusion analysis (MDA) has been developed as a new non-destructive evaluation methodology to monitor the strength degradation of graphite-epoxy composite materials. Studies of composite strength degradation due to high moisture identify reversible strength loss due to current moisture content and irreversible strength loss related to prior moisture exposure with microstructure damage...
متن کاملPhysical properties of resin-modified glass-ionomers.
The physical properties and shear bond strength of two resin-modified glass-ionomers: RMGIs (FJL and VT) and as a control, a conventional glass-ionomer: CGI (FJ), were evaluated. Ninety percent of the setting shrinkage under dry conditions and nominal hygroscopic expansion in water during 360 h occurred within the first 24 h. The nominal hygroscopic expansion of CGI was 0.38% while the RMGIs de...
متن کاملinvestigation of thermal comfort properties of woven sport fabric using blend of estabragh fibers
امروزه لباس در نظر ورزشکاران و کسانی که برای اوقات فراغت خود و یا برای رسیدن به اندامی متعادل، ورزش می کنند؛ بسیار با اهمیت است. احساس مطلوب از لباس در زمره خصوصیات راحتی پوشش می باشد. خصوصیات انتقال رطوبت لباس، در ارزیابی راحتی حسی و حرارتی منسوجات تولید شده از آن ها بسیار مهم است. هدف از این تحقیق، معرفی پارچه جدید است که متشکل از الیاف استبرق با خواص منحصر به فرد می باشد. استبرق لیف طبیعی تو...
Shear bond strength evaluation of resin composite to resin-modified glass-ionomer cement using three different resin adhesives vs. glass-ionomer based adhesive
Background: The clinical success of sandwich technique depends on the strength of resin-modified glass ionomer cement (RMGIC) bonding to both dentin and resin composite. Therefore, the shear bond strength (SBS) of resin composite bonded to RMGIC utilizing different resin adhesives versus a GIC-based adhesive was compared. Materials and methods: In this in vitro study, 84 holes (5×2 mm) were pre...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 22 شماره 2
صفحات 205- 210
تاریخ انتشار 2009-08-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023