LOW TEMPERATURE MOLTEN SALT SYNTHESIS OF NANO CRYSTALLINE MgAl2O4 POWDER

نویسندگان

  • F. Golestani-Fard Center of Excellence for Advanced Materials and Processing (CEAMP), Iran University of Science and
  • F. Khorasanizadeh
  • M. Aminzare
  • S. Zhang 3 Department of Materials Engineering, University of Sheffield, Sheffield S1 3JD, UK.
  • Y. Safaei-Naeini 1 School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran.
چکیده مقاله:

Abstract: composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nanopowder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-Teller (BET) techniques. It was demonstrated that the formation temperature decreased to 850 particles revealed an average size of 30 nm with a narrow size distribution. The mechanism of MgAlwas found to be a template type where the morphology and size of product were similar to those of alumina formedfrom boehmite decomposition. Prolonging the reaction time from 0.5 to 3 h, the reaction was further completed andcrystallinity was improved. However, the increase of temperature was more effective in this regard.MgAl2O4 (MA) nano powder was synthesized via molten salt technique, by heating stochiometric°C. The nano spinel2O4 formation

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Low temperature synthesis of CaZrO3 nanoceramics from CaCl2–NaCl molten eutectic salt

CaZrO3 nanoceramics were successfully synthesized at 700 C using the molten salt method, and the effects of processing parameters, such as temperature, holding time, and amount of salt on the crystallization of CaZrO3 were investigated. CaCl2, Na2CO3, and nano-ZrO2 were used as starting materials. On heating, CaCl2–NaCl molten eutectic salt provided a liquid medium for the reaction of CaCO3 an...

متن کامل

LOW TEMPERATURE SYNTHESIS OF NANOCRYSTALLINE MgAl2O4 SPINEL VIA SUCROSE PROCESS

Abstract: Nanocrystalline MgAl2O4 spinel powder was synthesized using metal nitrates and a polymer matrix-based composed of sucrose and polyvinyl alcohol (PVA). The precursor and the calcined powders were characterized by simultaneous thermal analysis (STA), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and scanning electron microscopy (SEM). According to XRD res...

متن کامل

low temperature synthesis of cazro3 nanoceramics from cacl2–nacl molten eutectic salt

cazro3 nanoceramics were successfully synthesized at 700 c using the molten salt method, and the effects of processing parameters, such as temperature, holding time, and amount of salt on the crystallization of cazro3 were investigated. cacl2, na2co3, and nano-zro2 were used as starting materials. on heating, cacl2–nacl molten eutectic salt provided a liquid medium for the reaction of caco3 an...

متن کامل

EFFECT OF ZrO2 PARTICLE SIZE ON MORPHOLOGY and SYNTHESIS OF NANO CaZrO3Via MOLTEN SALT METHOD

Well crystallized pure calcium zirconate (CaZrO3 ) nanopowder was successfully synthesized using the molten-salt method. CaCl2 , Na 2CO3, micro-ZrO 2and nano-ZrO 2 were used as starting materials. On heating, Na2CO3 reacted with CaCl 2to form NaCl and CaCO 3. Nano CaZrO 3 was formed by reacting equimolar amounts of in situformed CaCO 3 (or CaO) and ZrO 2 in molten Na 2CO3-NaCl e...

متن کامل

Low-temperature synthesis route for YBa2Cu3Ox powder

• A submitted manuscript is the author's version of the article upon submission and before peer-review. There can be important differences between the submitted version and the official published version of record. People interested in the research are advised to contact the author for the final version of the publication, or visit the DOI to the publisher's website. • The final author version ...

متن کامل

Mechano-chemical activation of MoO3-CuO/C powder mixture to synthesis nano crystalline Mo-Cu alloy

In this study, a high energy planetary ball milling technique was used to synthesize nano-crystalline Mo-Cu alloys. Molybdenum trioxide (MoO3) and copper oxide (CuO) were used as the starting materials. Carbo-thermal co-reduction of mixed Mo and Cu oxides powders was done with milling followed by a heat treatment at a high temperature. Differential thermal analysis/thermogravimetric (DTA/TG) wa...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 8  شماره 3

صفحات  23- 28

تاریخ انتشار 2011-09

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023