High porosity polyethylene aerogels

نویسندگان

  • Christophe Daniel Dipartimento di Chimica e Biologia e Unità INSTM, Università degli Studi di Salerno Via Giovanni Paolo II,132- 84084 Fisciano (SA), Italy
  • Gaetano Guerra Dipartimento di Chimica e Biologia e Unità INSTM, Università degli Studi di Salerno Via Giovanni Paolo II,132- 84084 Fisciano (SA), Italy
  • Simona Longo Dipartimento di Chimica e Biologia e Unità INSTM, Università degli Studi di Salerno Via Giovanni Paolo II,132- 84084 Fisciano (SA), Italy
چکیده مقاله:

Monolithic aerogels of high molecular weight polyethylene (Mw= 3x106- 6x106 g/mol) have been prepared by solvent extraction with supercritical carbon dioxide from thermoreversible gels prepared in decalin. These low density and highly porous aerogels present an apparent porosity up to 90%. The aerogel morphology observed by scanning electron microscopy (SEM) is characterized by spherulitic structures being interconnected by fibers. X-ray diffraction experiments show that PE aerogels are highly crystalline with a degree of crystallinity of c.a. 80% and PE chains being packed into the typical orthorombic unit cell. Combined SEM and N2 sorption investigations show that PE aerogels are essentially macroporous with a small amount of mesopores. The oil-sorption performance of polyethylene aerogels has been also evaluated in this study in order to assess a possible use of these materials for oil spillage recovery and results show that aerogel macropores allow a very fast sorption kinetics with a 100% oil weight uptake obtained in less than 1 minute.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

high porosity polyethylene aerogels

monolithic aerogels of high molecular weight polyethylene (mw= 3x106- 6x106 g/mol) have been prepared by solvent extraction with supercritical carbon dioxide from thermoreversible gels prepared in decalin. these low density and highly porous aerogels present an apparent porosity up to 90%. the aerogel morphology observed by scanning electron microscopy (sem) is characterized by spherulitic stru...

متن کامل

Solvent-tuned hierarchical porosity in nitrocellulose aerogels.

We describe the simple preparation of nitrocellulose gels and high surface area (300 + m(2) g(-1)) aerogels and their hierarchical pore structures. The solvent in which the gels form greatly influences the pore geometry and size distribution of the gels in both the macro- and mesopore domains.

متن کامل

1 3 Se p 20 05 NMR measurements of hyperpolarized 3 He gas diffusion in high porosity silica aerogels

Hyperpolarized He is used to nondestructively probe by NMR the structure of custom-made and commercial silica aerogels (97% and 98.5% porous). Large spin-echo signals are obtained at room temperature and very low magnetic field (2 mT) even with small amounts of gas. Attenuation induced by applied field gradients results from the combined effects of gas diffusion and confinement by the porous me...

متن کامل

Synchrotron Microtomography Reveals the Fine Three-Dimensional Porosity of Composite Polysaccharide Aerogels

This study investigates the impact of ice-templating conditions on the morphological features of composite polysaccharide aerogels in relation to their mechanical behavior and aims to get a better insight into the parameters governing these properties. We have prepared polysaccharide aerogels of guar galactomannan (GM) and tamarind seed xyloglucan (XG) by enzymatic oxidation with galactose oxid...

متن کامل

The control of porosity at nano scale in resorcinol formaldehyde carbon aerogels

Organic aerogels were synthesized by sol–gel polymerization of resorcinol (R) with formaldehyde (F) catalyzed by sodium carbonate (C) followed by vacuum drying. The influence of the resorcinol/sodium carbonate ratio (R/C) on the porous structure of the resultant aerogels was investigated. The nitrogen adsorption–desorption measurements show that the aerogels possess a well developed porous stru...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 2  شماره 1

صفحات  49- 55

تاریخ انتشار 2015-01-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023