Damage of tungsten due to helium and argon ions of a PF device was studied. Tungsten samples were irradiated by 20 shots of the plasma focus device with argon and helium as working gases, separately. The tungsten surface was analyzed by SEM, before and after irradiation. SEM revealed dense blisters with diameters of a few hundred nanometers, on the samples which were irradiated by helium ions, while on the samples irradiated by argon, cracks were developed on the surface. XRD analysis was used for crystallography of tungsten, before and after irradiation. Irradiation by helium and argon affects peak location, peak intensity, FWHM, and spacing of planes, which shows that the crystalline structure of tungsten is affected by irradiation.Characteristics of ion beam of the plasma focus device were calculated by the Lee code. The depth profiles of dpa/shot and ion concentration were calculated using the SRIM code. Using the Lee code, the average fluencies of helium and argon ion beams of the PF device were calculated about 7.9×1014 cm-2 and 0.25×1014 cm2 per shot, respectively. SRIM revealed that the maximum DPA was about 1.7 and 0.17 and occur in the depth of 7 nm and 30 nm for argon and helium, respectively. Also, the maximum concentration occurs in the depth of 20 nm and 40 nm for argon and helium, respectively.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of ion flux on helium retention in helium-irradiated tungsten

Helium retention in irradiated tungsten leads to swelling, pore formation, sample exfoliation and embrittlement with deleterious consequences in many applications. In particular, the use of tungsten in future nuclear fusion plants is proposed due to its good refractory properties. However, serious concerns about tungsten survivability stems from the fact that it must withstand severe irradiatio...

متن کامل

Studies on argon collisions with smooth and rough tungsten surfaces.

The aim of this work is to investigate argon scattering behaviors on the smooth and rough tungsten surfaces. Current work deals with numerical simulation of nanoscale heat transfer process accompanying with rarefied gas-solid substrate interactions using molecular dynamics (MD) method. Taking into account that this method is very time consuming, MD simulation using CUDA capable Graphic Cards is...

متن کامل

Influence of Gliding Arc Cold Plasma Based on Argon, Helium and Compact Air on Bactria Around the Wound: Experimental Investigation

Background: Today, the use of cold plasma and its applications have taken into consideration. The plasma is a mixture of active oxygen and negative ions. This compound has a practical effect on the elimination of all types of bacteria and viruses. The cold plasma feature is essential and very useful in disinfecting processes. In this investigation, we plan to study the effect of gliding arc pla...

متن کامل

In Vitro and in Vivo studies of the Effects of Cold Argon Plasma on Decreasing the Coagulation Time

Introduction Cold plasma is a self-sterilized, painless, and non-contact method in surgeries. These properties allow it to be applied to the living tissues and heat-sensitive parts. The aim of this study was to design a new cold plasma producer device and evaluate the effects of cold argon plasma on decreasing the coagulation time of blood drop in vitro and that of the injured liver blood in vi...

متن کامل

Argon and helium plasma coagulation of porcine liver tissue

Objective Argon plasma coagulation (APC) and helium plasma coagulation (HPC) are electrosurgical techniques that provide noncontact monopolar electrothermal haemostasis. Although these techniques have been widely used clinically during the last three decades, their in vivo effects on liver tissue remain unclear. Methods We investigated the effects of different power levels (10-100 W) of APC and...

متن کامل

Surface damage in ultrafine and multimodal grained tungsten materials induced by low energy helium irradiation

SEMmicrograph of a multimodal grained tungsten material after being irradiated with 200 eV He ions at 950 C and a fluence of 1 10 m 2 showing the detachment and the nanostructuring of the small grains as well as pore formation on top of the nanostructures. The sample was etched before irradiation for better imaging of the grain boundaries. a r t i c l e i n f o

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 8  شماره 5

صفحات  1- 12

تاریخ انتشار 2020-09

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

کلمات کلیدی برای این مقاله ارائه نشده است

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023