In this research, the wear behavior of commercial grades of WC-10wt%Co (H10F), WC-40vol%Co and WC-40vol%FeAl-B composites with different amounts of boron from zero to 1000 ppm has been investigated by the pin on disk test  method at high temperature. The wear tests were done under load of 40 N, a distance of 100 m and at ambient temperature, 200 ̊C and 300 ̊C. Wear surfaces were examine...

بررسی رفتار سایشی کامپوزیت های wc-۱۰wt%co تجاری، wc-۴۰vol%co و wc-۴۰vol%feal-b در دمای محیط

در این پژوهش رفتار سایشی کامپوزیت های تجاری wc-10wt%co (h10f)، wc-40vol%co و کامپوزیت های wc-40vol%feal-b با مقادیر مختلف بور از صفر تا ppm1000 به روش پین روی دیسک بررسی شد. آزمون های سایش در دمای محیط، تحت بار 40 نیوتن و طی مسافت 100 متر انجام شدند. سطوح سایش به وسیله میکروسکوپ الکترونی روبشی (sem) مورد بررسی قرار گرفت. نتایج نشان داد که در بین نمونه ها، کامپوزیت wc-40vol%feal بدون بور کمترین ...

FRACTURE AND FATIGUE BEHAVIOR OF WC-Co AND WC-CoNi CEMENTED CARBIDES

The fracture and fatigue characteristics of several cemented carbide grades are investigated as a function of their microstructure. In doing so, the influence of binder chemical nature and content (Co and 76wt%Co-24wt%Ni), as well as carbide grain size on hardness, flexural strength, fracture toughness and fatigue crack growth (FCG) behavior is evaluated. Mechanical testing is combined with a d...

Geometric and Crystallographic Characterization of WC Surfaces and Grain Boundaries in WC-Co Composites

Electron backscattered diffraction has been used to determine the orientation of WC crystals in a WC-Co composite and atomic force microscopy has been used to measure the shapes of planar sections of the same crystals. A stereological analysis has been used to determine that { } 1010 prism facets and the {0001} basal planes are the WC surfaces that are most frequently in contact with Co. Furthe...

Effect of WC Concentration on Abrasive Wear Properties of the Thermally Sprayed WC -Ni Coatings

In this work the effects of WC concentration on abrasive wear behavior by thermally sprayed WC coating was evaluated using three body abrasive wear tester. A different combination of WC and NI coatings were deposited on steel substrates by flame spraying using powder with different WC concentrations (0 %, 12.5 %, 25 %, and 50 %). Flame torch was used for heating and coating of process. Microstr...

Technical Paper: Effectiveness of WC Fee Schedules