آثار مغناطوالاستیکی در آهنرباهای نانوکامپوزیتNd4Fe77.5B18.5

نویسندگان

چکیده مقاله:

  In this research, magnetostriction and thermal expansion of polymer-bonded Nd4Fe77.5B18.5 nano-composites are studied using strain gage method. The effect of sintering on samples is also studied. X-ray diffraction patterns and SEM pictures of the original and annealed samples show that the grain size of a -Fe and Fe3B soft magnetic phases in amorphous matrix increases and mechanical hardness of the samples improves after annealing at 700 ° C for 20 min.. Overall behavior of the thermal expansion is similar for samples in both cases, with about 20% larger coefficient for the annealed one. The magnetostriction measurements show huge magnitudes in order of 10-4 at the presence of relatively weak external magnetic fields. The magnitude of magnetostriction noticeably decreases after annealing which can originate from two different sources. Magnetostriction of the original sample mainly originates from single particle interactions of Nd-sublattice in Nd2Fe14B phase, but the situation is very different for the annealed sample. The complicate variations of the magnetostrictive isotherms of the annealed sample are discussed based on the following three factors,internal stresses, magnetocrystalline anisotropy and mechanisms of coercivity.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

آثار مغناطوالاستیکی در آهنرباهای نانوکامپوزیتnd<sub>۴</sub>fe<sub>۷۷.۵</sub>b<sub>۱۸.۵</sub>

در این تحقیق مغناطوتنگش و انبساط گرمایی نانوکامپوزیتهای nd4fe77.5b18.5 به هم بسته با پلیمر به روش پیمانه کرنشی مورد مطالعه قرار گرفته است. اثر بازپخت نمونه بر کمیتهای اندازه گیری شده نیز بررسی شده است. طرحهای پراش پرتو x به همراه تصاویر sem از نمونه اصلی و بازپخت شده نشان می دهند که بازپخت موجب رشد دانه فازهای مغناطیسی نرم α-fe و fe3b در زمینه آمورف و سختی مکانیکی نمونه می شود. رفتار عمومی منحن...

متن کامل

طراحی و ساخت پیچه‌ی هلمهولتز به منظور اندازه‌گیری آهنرباهای دائمی

شدت و جهت بردار مغناطش آهنرباهای دائمی بعد از ساخت، به دلایل گوناگونی، از شدت و جهت مطلوبی که حین ساخت مورد نظر بوده است اختلاف خواهند داشت. در این مقاله، مراحل طراحی فیزیکی و مکانیکی و سپس ساخت پیچه‌­ی هلمهولتز برای اندازه­‌گیری شدت و جهت بردار مغناطش در آهنرباهای دائمی به منظور استفاده در ساخت یک آندولاتور تخت برای اولین بار در کشور ارائه شده است. کالیبراسیون پیچه‌ی هلمهولتز با منبع جریان و پ...

متن کامل

اثر جانشانی کبالت بر خواص مغناطوالاستیکی ترکیب Cu13Fe6Nd

In this research the magnetoelastic properties of Nd6Fe13­-x­­Co­xCu (x = 0 and 1) intermetallic compoundes are investigated. Analysis of X-ray diffraction patterns indicates that a single phase is formed approximately for x = 0 and the x = 1 sample is multi-phase. The lattice parameters were decreased, the Néel temperature of main phase and the Curie temperature of impurity phase was increased...

متن کامل

اثر بربرین در تنظیم آستروسیتهای Gfap+ ناحیه هیپوکمپ موشهای صحرایی دیابتی شده با استرپتوزوتوسین

Background: Diabetes mellitus increases the risk of central nervous system (CNS) disorders such as stroke, seizures, dementia, and cognitive impairment. Berberine, a natural isoquinolne alkaloid, is reported to exhibit beneficial effect in various neurodegenerative and neuropsychiatric disorders. Moreover astrocytes are proving critical for normal CNS function, and alterations in their activity...

متن کامل

اثر بربرین در تنظیم آستروسیتهای Gfap+ ناحیه هیپوکمپ موشهای صحرایی دیابتی شده با استرپتوزوتوسین

Background: Diabetes mellitus increases the risk of central nervous system (CNS) disorders such as stroke, seizures, dementia, and cognitive impairment. Berberine, a natural isoquinolne alkaloid, is reported to exhibit beneficial effect in various neurodegenerative and neuropsychiatric disorders. Moreover astrocytes are proving critical for normal CNS function, and alterations in their activity...

متن کامل

ساختار بلوری، خواص مغناطیسی و مغناطوالاستیکی ترکیب‌های بین فلزی Nd6Fe13-xCoxCu

Influence of the partial substitution of Co for Fe on the structural, magnetic and magnetoelastic properties of Nd6Fe13Cu compounds are investigated. Analysis of X-ray diffraction patterns indicates that the multi-phase sample is formed for all samples. Upon Co substitution, the second phase Nd2Fe17, Nd2Fe17-yCoy with 0 < y < 1 and Nd2Fe17-zCoz with 1 < z < 2 is formed in the samples with x = 0...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 5  شماره 1

صفحات  17- 27

تاریخ انتشار 2005-06

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

کلمات کلیدی برای این مقاله ارائه نشده است

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023