Morakabati, M.
Malek Ashtar University.
[ 1 ] - Investigation of the Effect of Homogenization Treatment on Distribution of Alloying Elements, Microstructure and Hardness of Co-Al-W-Ti-Ta-Base Superalloy
The aim of this study was to investigate the effect of temperature and time of homogenization treatment on the microstructure, distribution of alloying elements and hardness of the novel Co-based superalloy Co-7Al-7W-4Ti-2Ta. For this purpose, the specimens were first homogenized at 1250 and 1300 °C for 2, 4, 6 and 8 hours and then water-cooled. Subsequently, the specimens were subjected to har...
[ 2 ] - Determining the Hot Deformation Temperature Range of Medium Carbon Ni-Cr-Mo Low Alloy Steels using Hot Tensile and Hot Torsion Tests
The aim of this study was to investigate the suitable temperature range for hot deformation of three medium carbon Ni-Cr-Mo low alloy steels by hot tensile and hot torsion tests. Hot tensile tests were carried out in the te,prature range of 850-1150°C at a constant strain rate of 0.1 s-1 until fracture. Then, the tensile flow behavior, hot ductility and microstructural evolution of the steels w...
[ 3 ] - EVALUATING HOT DEFORMATION BEHAVIOR OF W360 TOOL STEEL BY HOT COMPRESSION TEST
In this research, the hot deformation behavior of W360 tool steel was investigated using hot compression test at 1000-1200°C and strain rates of 0.001, 0.01, 0.1, and 1 s-1. According to the results, dynamic recrystallization was found the most important restoration factor of this alloy during hot deformation. Recrystallization was enhanced with an increase in temperature and strain rate. Also,...