[ 2 ] - Structural Evolution of Al-20% (wt) Al2O3 System during Ball Milling Stages
Production of nanostructured aluminum matrix composite powder by high energy ball milling is investigated. Scanning electron microscopy analysis as well as the tap and green density measurements were used to optimize the milling time needed for the completion of the mechanical milling process. Also, we studied the particles morphology and size distribution change with milling time and its corre...
[ 3 ] - Synthesis of TiC-Al2O3 Nanocomposite from Impure TiO2 by Mechanical Activated Sintering
In this research, the production possibility of TiC-Al2O3 nanocomposite, as a useful ceramic from commercially pure TiO2, aluminum powder and carbon black has been investigated. Routile (TiO2) with carbon black and aluminum were placed in a high energy ball mill and sampled during different milling times. Then, the activated powders were synthesized at different temperatures in an atmosphere co...
[ 4 ] - Hydrothermal Synthesis of Aligned Hydroxyapatite Nanorods with Ultra-High Crystallinity
Hydroxyapatite nanorods aligned with ultrahigh crystallinity and high-yield were successfully synthesized through a hydrothermal approach. In this experiment, a new composition of cetyltrimethylammonium bromide ((CH3(CH2)15N+(CH3)3Br-) was designated as CTAP)/Ca(NO3)2/(NH4)2HPO4/NaOH and distilled water under hydrothermal condition, to synthesize single crystalHAp nanorods with diameter of 20 ±...
[ 5 ] - Tribological Behavior of Reinforced and Unreinforced High Chromium Cast Iron
In this paper, the metal matrix composites containing 22 wt % Cr, 2.5 wt % C and 2 to 16 volume percent TiC were processed by solidifying Fe-Cr-Ti-C in which precipitation of titaniumcarbide and chromium carbide occurred. The microstructure and abrasion resistance of in-situ synthesized composites were compared with the unreinforced high chromium white cast iron (HCWCI) containing 22 w. t. % C...