TEM Characterization and Properties of Cu-1 wt.% TiB2 Nanocomposite Prepared by Rapid Solidification and Subsequent Heat Treatment
Authors
Abstract:
Copper matrix composite reinforced by 1wt.% TiB2 particles was prepared using in situ reaction of Cu-1.4wt.% Ti and Cu-0.7wt.% B by rapid solidification and subsequent heat treatment for 1-20 hrs at 900ºC. High-resolution transmission electron microscopy (HRTEM) characterization showed that primary TiB2 particles were formed in liquid copper. Heat treatment of as-solidified samples led to the formation of secondary TiB2 particles via spinodal decomposition of titanium-rich zone inside the grains. Mechanical properties (after 50% reduction in area) as well as electrical conductivity of composite were evaluated after heat treatment and were compared with those of pure copper. The results indicated that, due to the formation of secondary TiB2 particles in the matrix, electrical conductivity increased along with hardness up to 10 hrs of heat treatment and reached 65% IACS and 155 HV, respectively. Moreover, the maximum ultimate (i.e. 580 MPa) and yield (i.e. 555 MPa) strengths of composite were achieved at this time.
similar resources
tem characterization and properties of cu-1 wt.% tib2 nanocomposite prepared by rapid solidification and subsequent heat treatment
copper matrix composite reinforced by 1wt.% tib2 particles was prepared using in situ reaction of cu-1.4wt.% ti and cu-0.7wt.% b by rapid solidification and subsequent heat treatment for 1-20 hrs at 900ºc. high-resolution transmission electron microscopy (hrtem) characterization showed that primary tib2 particles were formed in liquid copper. heat treatment of as-solidified samples led to the f...
full textarchitecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولsome properties of fuzzy hilbert spaces and norm of operators
in this thesis, at first we investigate the bounded inverse theorem on fuzzy normed linear spaces and study the set of all compact operators on these spaces. then we introduce the notions of fuzzy boundedness and investigate a new norm operators and the relationship between continuity and boundedness. and, we show that the space of all fuzzy bounded operators is complete. finally, we define...
15 صفحه اولMicrostructural Evolution of Copper-Titanium Alloy during In-situ Formation of TiB2 Particles
Bulk Cu-Ti alloy reinforced by TiB2 nano particles was prepared using in-situ reaction between Cu3.4wt.% Ti and Cu-0.7wt.% B along with rapid solidification and subsequent heat treatment for 1-10 hrs at 900oC. High-resolution transmission electron microscopy (HRTEM) characterization showed that primary TiB2 nano particles and TiB whiskers were formed by in-situ reaction between Ti and B in the ...
full textMy Resources
Journal title
volume 2 issue 4
pages 519- 526
publication date 2012-12-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023