SYNTHESIS, MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Mg - 5Zn - 0.3Ca/nHA NANOCOMPOSITES
Authors
Abstract:
Recently, magnesium and its alloys have attracted great attention for use as biomaterial due to their good mechanical properties and biodegradability in the bio environment. In the present work, nanocomposites of Mg - 5Zn - 0.3Ca/ nHA were prepared using a powder metallurgy method. The powder of Mg, Zn and Ca were firstly blended, then four different mixtures of powders were prepared by adding nHA in different percentages of 0, 1, 2.5 and 5 %wt. Each mixture of powder separately was fast milled, pressed, and sintered. Then, the microstructure and mechanical properties of the fabricated nanocomposites were investigated. The XRD profile for nanocomposites showed that the intermetallic phases of MgZn2, MgZn5.31 and Mg2Ca were created after sintering and the SEM micrographs showed that the grain size of nanocomposite reduced by adding the nHA. The nano composite with 1wt. % nHA increased the density of Mg alloy from 1.73 g/cm3 to 1. 75 g/cm3 by filling the pores at the grain boundaries. The compressive strength of Mg alloy increased from 295MPa to 322, 329 and 318MPa by addition of 1, 2.5 and 5wt. % nHA, respectively.
similar resources
determination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولmicrostructure and mechanical properties of al2o3-sic nanocomposites with 0.05% mgo and different sic volume fraction
abstract: in this study, al 2 o 3 –sic nanocomposites have been fabricated by mixing of alumina powder containing 0.05% weight magnesium oxide and silicon carbide nano powders, followed by hot pressing at 1650 0 c. the mechanical properties of al 2 o 3 -sic nanocomposites containing different volume fraction (2.5, 5, 7.5, 10 and 15%) of nano scale sic particles were investigated and compared wi...
full textSynthesis and mechanical properties of nanostructured Mg-Al-Nd alloys
In this work, nanostructured Mg-Al-Nd alloys were successfully fabricated using mechanical alloying method. Phase structures of the milled powders and the extruded rods were examined using X-ray diffraction (XRD) and the microstructures were observed using a transmission electron microscope (TEM). The element distributions were also examined by an energy dispersive spectroscopy (EDS) system. Th...
full textNanocrystalline forsterite for biomedical applications: synthesis, microstructure and mechanical properties.
Forsterite (Mg2SiO4) because of its exceptionally high fracture toughness which is close to that of cortical bones has been nominated as a possible successor to calcium phosphate bioceramics. Recent in vitro studies also suggest that forsterite possesses good bioactivity and promotes osteoblast proliferation as well as adhesion. However studies on preparation and sinterability of nanocrystallin...
full textSynergetic Effect of Graphene and MWCNTs on Microstructure and Mechanical Properties of Cu/Ti3SiC2/C Nanocomposites
Multi-walled carbon nanotubes (MWCNTs) and graphenes have been taken for novel reinforcements due to their unique structure and performance. However, MWCNTs or graphenes reinforced copper matrix composites could not catch up with ideal value due to reinforcement dispersion in metal matrix, wettability to metal matrix, and composite material interface. Taking advantage of the superior properties...
full textMy Resources
Journal title
volume 14 issue 4
pages 58- 68
publication date 2017-12
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023