Synthesis and Characterization of Nanocrystalline Ni3Al Intermetallic during Mechanical Alloying Process
Authors
Abstract:
In this research, formation of nanocrystalline Ni3Al intermetallic from Ni and Al elemental powders by mechanical alloying (MA) process and its characterization was investigated. Therefore, the evolutions in microstructure such as phase transformation, oxidation in air and introduction of Fe impurity from milling media after MA were evaluated using XRD, Rietveld refinement, TEM, SEM, EDS and ICP analyses. Milling after 4 h resulted in formation of Ni3Al/Al2O3 composite in air while continuing milling time up to 8 h resulted in obtaining Ni3Al product. TEM observations along with XRD combined Rietveld’s refinement analysis confirmed the existence of a disorder structure and nanocrystals of Ni3Al embedded in an amorphous matrix after 16 hours of milling. Moreover, the lattice parameter of Ni3Al product and Fe contamination of powder were increased by increasing milling time.
similar resources
Synthesis and Characterization of Nanocrystalline Ni50Al50-xMox (X=0-5) Intermetallic Compound During Mechanical Alloying Process
In the present study, nanocrystalline Ni50Al50-xMox (X = 0, 0.5, 1, 2.5, 5) intermetallic compound was produced through mechanical alloying of nickel, aluminum, and molybdenum powders. AlNi compounds with good and attractive properties such as high melting point, high strength to weight ratio and high corrosion resistance especially at high temperatures have attracted the attention of many rese...
full textsynthesis and characterization of nanocrystalline ni50al50-xmox (x=0-5) intermetallic compound during mechanical alloying process
in the present study, nanocrystalline ni50al50-xmox (x = 0, 0.5, 1, 2.5, 5) intermetallic compound was produced through mechanical alloying of nickel, aluminum, and molybdenum powders. alni compounds with good and attractive properties such as high melting point, high strength to weight ratio and high corrosion resistance especially at high temperatures have attracted the attention of many rese...
full textFormation Mechanism and Enthalpy of Mixing of Nanocrystalline NiTi Intermetallic during Mechanical Alloying
full text
Formation Mechanism and Enthalpy of Mixing of Nanocrystalline NiTi Intermetallic during Mechanical Alloying
full text
Eddy Current and Microwave Characterization of (fe65co35)70al30 Nanocrystalline Alloy Synthesized by Mechanical Alloying Process
An investigation was conducted to explore the applicability of eddy current and microwave techniques to characterize grains size variation during mechanical alloying. A series of Nanocrystalline (Fe65Co35)70Al30 samples have been prepared, these structures are prepared using mechanical alloying based on planetary ball mill under several milling conditions. Mechanical alloying is a non-equilibri...
full textsynthesis and characterization of some macrocyclic schiff bases
ماکروسیکلهای شیف باز از اهمیت زیادی در شیمی آلی و دارویی برخوردار می باشند. این ماکروسیکلها با دارابودن گروه های مناسب در مکانهای مناسب می توانند فلزاتی مثل مس، نیکل و ... را در حفره های خود به دام انداخته، کمپلکسهای پایدار تولید نمایند. در این پایان نامه ابتدا یک دی آلدئید آروماتیک از گلیسیرین تهیه می شود و در مرحله بعدی واکنش با دی آمینهای آروماتیک و یا آلیفاتیک در رقتهای بسیار زیاد منجر به ت...
15 صفحه اولMy Resources
Journal title
volume 25 issue 2
pages 89- 98
publication date 2012-06-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023