Structural Investigation, Physical and Optical Properties of Mixed Alkali Bismuth Borate Glasses
Authors
Abstract:
Lead free, eco-friendly bismuth borate glasses doped with alkali oxides of composition xLi2O+(30-x)Na2O+55B2O3+15Bi2O3 (x = 5,10,15,20,25) were prepared by melt quenching technique. Amorphous nature of glasses was confirmed by X-ray diffraction. Density measurements were carried out at room temperature by standard principle of Archimedes with Xylene as an immersion liquid. The non-linear behavior of density, molar volume, glass transition temperature, direct and indirect optical band gaps confirm the mixed alkali effect. The FTIR analysis revealed that the network structure consists of BO3, BO4 units and BiO6 octahedral units. UV-vis spectroscopy shows no sharp absorption edges giving a clear indication of the amorphous nature of the glasses.
similar resources
Optical and Thermal Properties of Mixed Alkali Phosphate Based Glasses
Glassy samples with a composition of 40P2O5–30V2O5–(30-x)Li2O– xK2O, 0<x<30 (mol %) were prepared by the conventional melt quenching technique in two forms of bulk and blown film. X-ray diffraction patterns corroborated the amorphous feature of the samples. Density of samples was investigated by using Archimedes principle. Based on absorption and reflection spectra, indirect a...
full textMechanical Properties of Alkali Borate Glasses
A GLASS is, formally, a solid that solidifies without a well-defined melting point— defined as a singular temperature at which there occurs a discontinuous change in a physical property, for example specific volume, during transition between a liquid state and its corresponding solid state—but instead exhibits a continuous change in that property over a range of temperature. Glasses tend to inh...
full textOptical Basicity and Polarizability of Nd3+-Doped Bismuth Borate Glasses
This paper reports on different physical and optical properties of Nd3+-doped bismuth borate glasses. The glasses containing Nd3+ in (25 − x)Bi2O3:20Li2O:20ZnO:35B2O3:xNd2O3 (where x = 1, 1.5, 2 mol%) have been prepared by melt-quenching method. The amorphous nature of the glasses was confirmed by X-ray diffraction studies. The physical parameters like dielectric constant, refractive index, ion...
full textDoped Zinc Lithium Bismuth Borate Glasses
Zinc lithium bismuth borate glasses containing Er in (25x): Bi2O3:20Li2O:20ZnO: 35B2O3:xEr2O3 (where x=1, 1.5,2 mol %) have been prepared by melt-quenching method. The amorphous nature of the glasses was confirmed by x-ray diffraction studies. Optical absorption and fluorescence spectra were recorded at room temperature for all glass samples. Judd-Ofelt intensity parameters Ωλ (λ=2, 4, 6) are e...
full textions doped zinc bismuth borate glasses
Glasses having composition 20ZnO·xBi2O3·(79-x)B2O3 (15 x 35, in mol%) doped with 1 mol% of Nd 3+ ions were prepared. The different physical and absorption spectral properties have been investigated to understand the variation of the hypersensitive absorption band intensities. From the absorption spectra, Judd-Ofelt intensity parameters, ( = 2, 4, 6) have been calculated and these parameters wer...
full textdetermination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولMy Resources
Journal title
volume 3 issue 3
pages 1- 7
publication date 2017-08-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023