MICROSTRUCTURE STUDY ON AL-5%SiC NANOCOMPOSITE POWDERS
Authors
Abstract:
Abstract: In this study Al-5 (Vol) % SiCp nanocomposite powder has been successfully synthesized by high-energy planetary milling of Al and SiC powders for a period of 25 h at a ball-to-powder ratio of 15:1. The changes of the lattice strain, the crystallite size of the matrix phase, and the nanocomposite powder microstructure with time have been investigated by X-ray diffraction (XRD), X-ray mapping, and scanning electron microscopy (SEM) analyses. The morphologies of the nanocomposite powders obtained after 25 h of milling have also been studied by transmission electron microscopy (TEM). The results showed that nanocomposite powders were composed of near-spherical particles and, moreover, the SiC particles were uniformly distributed in the aluminum matrix.
similar resources
Effect of Mechanical Milling on the Morphologyand Structural Evaluation of Al-Al2O3 Nanocomposite Powders
The morphological and microstructural changes during mechanical milling of Al powder mixed with 2.5, 5 and 10 wt.% Al2O3 particles were studied. The milling was performed in a planetary ball mill for various times up to 20 h. The produced composite powders were investigated using X-ray diffraction pattern (XRD) to elucidate the role of particle size, secondary phase content and milling time on ...
full textManufacturing Carbon Nanotube/PVDF Nanocomposite Powders
Aprocedure for the production of carbon nanotube (CNT) reinforced poly(vinylidine difluoride) (PVDF) powders has been developed. These powders are versatile precursors for a range of nanocomposite materials. The morphology of the CNT/PVDF powder can be related to the interaction between filler and matrix, which depends on the degree of modification of the polymer with grafted maleic anhydride (...
full textNanocomposite mullite/mullite powders by spray pyrolysis
A mullite/mullite nanocomposite powder has been synthesized, composed of nanometer-size 3Al2O3 · 2SiO2 (‘3 : 2’) mullite precipitates within a matrix of the high alumina 2Al2O3 · SiO2 (‘2 : 1’) mullite. Historically, the transition from the metastable high-alumina phase to the thermodynamically stable ‘3 : 2’ phase of mullite has been thought to be a continuous process, involving a continuous s...
full textMicrostructure and mechanical properties of nanocomposite (Ti,Si,Al)N coatings
In this work (Ti,Si,Al)N films were deposited using only rf or a combination of rf and d.c. reactive magnetron sputtering. Chemical composition, thickness, film structure and mechanical properties of the films were investigated by means of Rutherford backscattering (RBS), electron microprobe analysis (EPMA), ball-cratering, X-ray diffraction (XRD) and ultramicroindentation, respectively. All sa...
full textStudy on Microstructure and Mechanical Properties of Hypereutectic Al–18Si Alloy Modified with Al–3B
An hypereutectic Al-18Si alloy was modified via an Al-3B master alloy. The effect of the added Al-3B and the modification temperature on the microstructure, tensile fracture morphologies, and mechanical properties of the alloy were investigated using an optical microscope, Image-Pro Plus 6.0, a scanning electron microscope, and a universal testing machine. The results show that the size of the ...
full textMicrostructure Characteristics of Ultra-fine ZrO2-Y203 Ceramic Powders*
Yttria-doped zirconia powders" with an extremely small crystallite size (8 nm) and a narrow size distribution have been prepared by gel precipitation methods. Precipitation of an alkoxide solution in water ("alkoxide" synthesis) results in weaker agglomerates when compared with a precipitation of a metal chloride solution in ammonia ("chloride" synthesis). Both types of agglomerate are fracture...
full textMy Resources
Journal title
volume 8 issue 1
pages 32- 39
publication date 2011-03
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023