Investigation of Macroporous Calcium Phosphate Cement Obtained by Foamed Gelatin Polymer
Authors
Abstract:
This study deals with the effect of gelatin on physical and mechanical properties of calcium phosphate bone cements. The mixture of tetracalcium phosphate (TTCP) and dicalcium phosphate (DCPA) as the cement powder was mixed with 6 wt% Na2HPO4 solution containing different amount (0, 2, 5 and 8% in w/w) of foamed gelatin as liquid phase. The physical properties were determined in the terms of setting time and macroporosity. The compressive strength was also checked before and after soaking the cements in simulated body fluid (SBF). The phase composition, microstructure and chemical groups were respectively determined using X-ray diffraction (XRD), Scanning electron microscopy (SEM) and Fourier transformation Infrared Spectroscopy (FTIR). The results showed that gelatin accelerated hydroxyapatite (HA) precipitation during setting and reduced the initial setting time from 35 min for cement without gelatin to 23 min for cement with the most amount of gelatin. Moreover, 17% (in v/v) macroporosity was induced in the cement structure using 8% solution of gelatin as the cement liquid. Gelatin addition promoted compressive strength of the set cement from 1.13 MPa (for gelatin-free cement) to 5.8 MPa.
similar resources
Injectable and macroporous calcium phosphate cement scaffold.
Calcium phosphate cement (CPC) can be molded and self-hardens in vivo to form resorbable hydroxyapatite with excellent osteoconductivity. The objective of this study was to develop an injectable, macroporous and strong CPC, and to investigate the effects of porogen and absorbable fibers. Water-soluble mannitol was used as porogen and mixed with CPC at mass fractions from 0% to 50%. CPC with 0-4...
full textIntroduction of gelatin microspheres into an injectable calcium phosphate cement.
For tissue engineered bone constructs, calcium phosphate cement (CPC) has a high potential as scaffold material because of its biocompatibility and osteoconductivity. However, in vivo resorption and tissue ingrowth is slow. To address these issues, microspheres can be incorporated into the cement, which will create macroporosity after in situ degradation. The goal of this study was to investiga...
full textCALCIUM PHOSPHATE CEMENT: STUDY OF (BETA-TRICALCIUM PHOSPHATE, DICALCIUM PHOSPHATE AND CALCIUM CARBONATE SYSTEM
Calcium phosphate cements (CPCs), using B-tricalcium phosphate (ß-TCP, Ca3 (P04)2), dicalcium phosphate (DCP, CaHP04), calcium carbonate (Ca CO3), and hydroxylapatite (HAp, Ca10(P04)6(OH)2) as powder cement and disodium hydrogen phosphate (Na2HP04) solution as liquid component were prepared. After mixing the powder and liquid constituents, injectable and self-setting calcium phosphate cements (...
full textStrengthening of calcium phosphate cement by compounding calcium carbonate whiskers.
The purpose of this study was to investigate how aragonite (calcium carbonate) whiskers influenced the strengthening and carbonating of alpha-tricalcium phosphate (alpha-TCP) based calcium phosphate cement. Aragonite whiskers of 0.95 microm width with an aspect ratio of 6.6 were prepared. The cement powder, alpha-TCP containing 0-50 mass% aragonite whisker, was mixed with 0.6 mol/L NaH2PO4 solu...
full textPreparation of an Injectable Macroporous α-TCP Cement
One of the most important characteristics of calcium phosphate cements is their resorbability when implanted in the body. However, the in vivo resorption rate is slow due to the lack of intrinsic open porosity. In this study, macroporous structures were obtained by mixing alpha-tricalcium phosphate (α-TCP) cement with a foamed liquid phase containing different concentrations of sodium hydrogen ...
full textMy Resources
Journal title
volume 2 issue 4
pages 18- 24
publication date 2016-11-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023