Increasing of tetragonal zirconia formation in the reaction sintering of alumina-zircon

Detection of tetragonal zirconia in alumina–zirconia powders by thermoluminescence

The thermoluminescence (TL) after excitation by UV or X-rays radiation of alumina-zirconia powders is investigated. The composites present five of the characteristic peaks of zirconia at −170, −145, −90, 0 and 95 °C. After a thermal treatment of mixed oxides, a new peak is observed at −35 °C in TL. This peak reveals the presence of stabilized tetragonal zirconia in the material. Moreover by com...

اصلاحیه: بررسی اثر افزودن ایتریا بر خواص کامپوزیت های مولایت -زیرکونیا ساخته شده به روش ریخته گری دوغابی

In this study, the effect of different amounts of Y2O3 on the properties of mullite-zirconia composites was investigated. For this purpose, these composites were fabricated by reaction-sintering of alumina and zircon as raw materials. Besides, the slip casting method was used for forming these composites, and sintering process was carried out at 1600 °C. Then, the physical and mechanical pro...

بررسی اثر افزودن ایتریا بر خواص کامپوزیت‏ های مولایت-زیرکونیای ساخته شده به روش ریخته‏ گری دوغابی

In this study, the effect of different amounts of Y2O3 on the properties of mullite-zirconia composites was investigated. For this purpose, these composites were fabricated by reaction-sintering of alumina and zircon as raw materials. Besides, the slip casting method was used for forming these composites, and sintering process was carried out at 1600 °C. Then, the physical and mechanical prope...

The Comparison of MgO and TiO2 Additives Role on Sintering Behavior and Microstructures of Reaction-Sintered Alumina-Zirconia-Mullite Composite

Alumina-Mullite-Zirconia ceramic composites were prepared by reaction sintering of alumina, zircon mixture and the sintering aids of magnesia and titania at temperatures of 1400 and 1600 C for 2 hours. The development of different phases and microstructures of the composites were analysed to assess the relative influence of the additives on the formation of alumina-zirconia-mullite compos...

formation and evolution of regional organizations: the case study of the economic cooperation organization (eco)

abstract because of the many geopolitical, geo economical and geo strategically potentials and communicational capabilities of eco region, members can expand the convergence and the integration in base of this organization that have important impact on members development and expanding peace in international and regional level. based on quality analyzing of library findings and experts interv...

Sintering of Zircon Powders