Enhanced Phtocatalytic Activity of α-Fe2O3 Nanoparticles Using 2D MoS2 Nanosheets
Authors
Abstract:
α‒Fe2O3/MoS2 nanocomposites were synthesized via hydrothermal method and characterized in terms of crystal structure, particle size and morphology, elemental purity and optical properties. Results confirmed the formation of α‒Fe2O3/MoS2 nanocomposites containing hematite nanoparticles with average diameter of 40 nm and MoS2 nanosheets with hexagonal crystal structure and sheet thickness of < 10 nm. Optical band gap measurements revealed decrease of the band gap of α‒Fe2O3 nanoparticles from 2.65 to 2.15 eV upon loading MoS2 nanosheets. The as‒synthesized α‒Fe2O3/MoS2 nanocomposites showed a high absorption capability in the visible irradiation. Photocatalytic examinations showed over 98 % degradation of Rhudamine Blue (Rh B) organic dye within 75 min. α‒Fe2O3/MoS2 nanocomposites enhanced the rate of degradation as compared to pure α‒Fe2O3 nanoparticles and MoS2 nanosheets.
similar resources
Ultrasmall Fe2O3 nanoparticles/MoS2 nanosheets composite as high-performance anode material for lithium ion batteries
Coupling ultrasmall Fe2O3 particles (~4.0 nm) with the MoS2 nanosheets is achieved by a facile method for high-performance anode material for Li-ion battery. MoS2 nanosheets in the composite can serve as scaffolds, efficiently buffering the large volume change of Fe2O3 during charge/discharge process, whereas the ultrasmall Fe2O3 nanoparticles mainly provide the specific capacity. Due to bigger...
full textHigh Efficient Photo-Fenton Catalyst of α-Fe2O3/MoS2 Hierarchical Nanoheterostructures: Reutilization for Supercapacitors
A novel three-dimensional (3D) α-Fe2O3/MoS2 hierarchical nanoheterostructure is effectively synthesized via a facile hydrothermal method. The zero-dimensional (0D) Fe2O3 nanoparticles guide the growth of two-dimensional (2D) MoS2 nanosheets and formed 3D flower-like structures, while MoS2 facilitates the good dispersion of porous Fe2O3 with abundant oxygen vacancies. This charming 3D-structure ...
full textSynthesis and Characterization of α-Fe2O3 Nanoparticles by Microwave Method
α-Fe2O3 (hematite) is the most stable iron oxide under ambient conditions. This transition metal oxide has been extensively investigated because it has unique electrical and catalytic properties. In this report, a novel microwave method for preparation of α-Fe2O3 nanoparticles has been developed. The process contained two steps: first, precursor were obtained from a mixed solution of 50 ml of 0...
full textPorous metallic MoO2-supported MoS2 nanosheets for enhanced electrocatalytic activity in the hydrogen evolution reaction.
Advanced materials for electrocatalytic water splitting are central to renewable energy research. In this work, MoS2 nanosheets supported on porous metallic MoO2 (MoS2/MoO2) were produced by sulfuration treatments of porous and highly conductive MoO2 for the hydrogen evolution reaction. Porous MoO2 with one-dimensional channel-like structures was prepared by calcination at elevated temperatures...
full textSynthesis, characterization and degradation activity of Methyl orange Azo dye using synthesized CuO/α-Fe2O3 nanocomposite
This study investigated the photo-degradation of methyl orange (MO) as a type of azo dye using a CuO/α-Fe2O3 nanocomposite. A CuO/α-Fe2O3 powder with a crystalline size in the range of 27-49 nm was successfully prepared using simple co-precipitation along with a sonication method. The characterization of the synthesized sample was done via XRD, FE-SEM, EDS, FTIR and DRS analyses. The Tauc equat...
full textFerromagnetism in freestanding MoS2 nanosheets
Freestanding MoS2 nanosheets with different sizes were prepared through a simple exfoliated method by tuning the ultrasonic time in the organic solvent. Magnetic measurement results reveal the clear room-temperature ferromagnetism for all the MoS2 nanosheets, in contrast to the pristine MoS2 in its bulk form which shows diamagnetism only. Furthermore, results indicate that the saturation magnet...
full textMy Resources
Journal title
volume 3 issue 4
pages 34- 40
publication date 2017-12-01
By following a journal you will be notified via email when a new issue of this journal is published.
Hosted on Doprax cloud platform doprax.com
copyright © 2015-2023