ساخت و بهینه‌سازی تمپلت‌های اکسید آلومینیوم جهت سنتز نانو‌سیم‌های فریت استرانسیوم و مقایسه آن با نانوپودرهای فریت استرانسیوم سنتز شده با روش سل- ژل

In this research, ordered porous anodic templates with 30 nm diameter and 15 µm thickness were prepared by using double anodization process. Dip coating method was employed to synthesize strontium ferrite in the form of nanowires in sol dilution. Ferrite nanopowders were also synthesized using sol gel method. The characterization of the nanostructures were examined by X-Ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM) and Energy Dispersive Spectroscopy (EDS). Hysteresis loops of nanopowders and nanowires, parallel and perpendicular to the wires axes, were measured by Superconducting Quantom Interference Device (SQUID). The results showed that double anodization in 0.3 M  oxalic acid at 4 oC with a single anodization for 12 hours could produce ordered template. Dip coating in 80 oC  for two hours could form fine and uniform strontium ferrite nanowires. The produced material showed parallel anisotropy.