the hydration products of a refractory calcium aluminate cement at intermediate temperatures

Authors

mohammad reza nilforoushan

nasrien talebian

abstract

the major hydraulic phase in all the calcium aluminate cements including ciment fondue is ca (caal2o4). once hydrated, it starts to form the hexagonal crystals of cah10 and c2ah8 that depending on the time and temperature of hydration convert to the cubic crystals of c3ah6 and ah3. the nature, sequence, crystallinity and microstructure of hydrated phases of commercial refractory calcium aluminate cement were analyzed using differential scanning calorimetry (dsc), differential thermal analysis (dta), x-ray diffraction (xrd) and scanning electron microscopy (sem). the results showed that the formation of different hydrated phases was temperature dependent. at 28 oc, the hydration products at the beginning of hydration were a gel phase, c2ah8 and gibbsite, while cah10 also formed after four days of hydration, both c2ah8  and cah10 were converted to  c3ah6 at latter ages. the rate of conversion of c2ah8 is dependent on the temperature  and  time  of  hydration  at  temperatures  higher  than  28 ºc  and  accelerates  with increasing temperature, but still takes several weeks for completion at 36 ºc.

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

The Hydration Products of a Refractory Calcium Aluminate Cement at Intermediate Temperatures

The major hydraulic phase in all the calcium aluminate cements including ciment fondue is CA (CaAl2O4). Once hydrated, it starts to form the hexagonal crystals of CAH10 and C2AH8 that depending on the time and temperature of hydration convert to the cubic crystals of C3AH6 and AH3. The nature, sequence, ...

full text

The Hydration Products of a Refractory Calcium Aluminate Cement at Low Temperatures

Calcium aluminates (CA) are the most important hydraulically setting cements used for preparing refractory castables, because they develop high strength at very early ages after placements.  The anhydrous phases of this kind of cements are CA, CA2 and traces of C12A7 and alpha-alumina. The major hydraulic phase in all of the CA cements including ciment fondu...

full text

the hydration products of a refractory calcium aluminate cement at low temperatures

calcium aluminates (ca) are the most important hydraulically setting cements used for preparing refractory castables, because they develop high strength at very early ages after placements.  the anhydrous phases of this kind of cements are ca, ca2 and traces of c12a7 and alpha-alumina. the major hydraulic phase in all of the ca cements including ciment fondue is ca. once hydrated, it starts to ...

full text

Limestone reaction in calcium aluminate cement–calcium sulfate systems

Article history: Received 18 June 2014 Accepted 7 May 2015 Available online xxxx

full text

Calculation of MnO Activity in Aluminate Slags at Various Temperatures

In this research, the activity of MnO, produced during steel making in aluminate-rich slags, was investigated. According to thermodynamic equations and mathematical calculation, a series of relations was obtained for evaluation of oxide activity using Masson’s theory. The obtained relations were solved according to Levenberg- Marquardt method and using Matlab software. The results were correlat...

full text

Effect of Tartaric Acid on Hydration of a Sodium-Metasilicate-Activated Blend of Calcium Aluminate Cement and Fly Ash F

An alkali-activated blend of aluminum cement and class F fly ash is an attractive solution for geothermal wells where cement is exposed to significant thermal shocks and aggressive environments. Set-control additives enable the safe cement placement in a well but may compromise its mechanical properties. This work evaluates the effect of a tartaric-acid set retarder on phase composition, micros...

full text

My Resources

Save resource for easier access later


Journal title:
iranian journal of chemistry and chemical engineering (ijcce)

Publisher: iranian institute of research and development in chemical industries (irdci)-acecr

ISSN 1021-9986

volume 26

issue 3 2007

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023