Characterization of Nanocrystalline Aluminum Alloy 5083 Powders Produced by Cryogenic Attrition
نویسنده
چکیده
منابع مشابه
Synthesis and Characterization of Nanocrystalline Ni50Al50-xMox (X=0-5) Intermetallic Compound During Mechanical Alloying Process
In the present study, nanocrystalline Ni50Al50-xMox (X = 0, 0.5, 1, 2.5, 5) intermetallic compound was produced through mechanical alloying of nickel, aluminum, and molybdenum powders. AlNi compounds with good and attractive properties such as high melting point, high strength to weight ratio and high corrosion resistance especially at high temperatures have attracted the attention of many rese...
متن کاملCryomilling of Aluminum-based and Magnesium-based Metal Powders
Ball milling has been shown to produce nanostructures in metal powders through severe repetitive deformation. Ball milling at cryogenic temperatures (cryomilling) is more effective in this capacity due to the low temperature by slowing recovery and minimizing diffusion distances between different components. Nanostructured metals are of interest because of their unique physical and mechanical p...
متن کاملStrain Rate Sensitivity Studies of Cryomilled Al Alloy Performed by Nanoindentation
Al 5083 alloy powder was mechanically milled in liquid nitrogen to achieve a nanocrystalline (NC) structure having an average grain size of 50 nm with high thermal stability, and then consolidated by quasi-isostatic (QI) forging. The consolidation resulted in ultrafine grains (UFG) of about 250 nm, and the bulk material exhibited enhanced strength compared to conventionally processed Al 5083. T...
متن کاملFriction stir welding of dissimilar joint of aluminum alloy 5083 and commercially pure titanium
In this study, commercially pure titanium and aluminum alloy 5083 in connection rotational speed of 1120 rpm and a feed rate of 50 mm per minute for butt welding by friction stir welding has been successfully completed. Micro-structure, hardness and tensile test was conducted on the connection. Welding area is a composite of aluminum and titanium particles that the particles plays an important ...
متن کاملMechanical properties of hot-pressed Al-4.5 wt. % Cu/WC composite
In this study, the elemental powders of aluminum and copper were initially subjected to mechanical alloying using an attrition ball mill under argon atmosphere to produce an Al-4.5 wt% Cu powder alloy. The WC nanoparticles were then added to the powder alloy and milled in a planetary ball mill to explore the role of the WC nanoparticles on the mechanical properties of the fabricated composite p...