Two-Layer Microstructures Fabricated by One-Step Anisotropic Wet Etching of Si in KOH Solution
نویسندگان
چکیده
Anisotropic etching of silicon in potassium hydroxide (KOH) is an important technology in micromachining. The residue deposition from KOH etching of Si is typically regarded as a disadvantage of this technology. In this report, we make use of this residue as a second masking layer to fabricate two-layer complex structures. Square patterns with size in the range of 15–150 μm and gap distance of 5 μm have been designed and tested. The residue masking layer appears when the substrate is over-etched in hydrofluoric acid (HF) solution over a threshold. The two-layer structures of micropyramids surrounded by wall-like structures are obtained according to the two different masking layers of SiO2 and residue. The residue masking layer is stable and can survive over KOH etching for long time to achieve deep Si etching. The process parameters of etchant concentration, temperature, etching time and pattern size have been investigated. With well-controlled two-layer structures, useful structures could be designed for applications in plasmonic and microfluidic devices in the future.
منابع مشابه
Etching characteristics of Si{110} in 20 wt% KOH with addition of hydroxylamine for the fabrication of bulk micromachined MEMS
Anisotropic wet etching is a most widely employed for the fabrication of MEMS/NEMS structures using silicon bulk micromachining. The use of Si{110} in MEMS is inevitable when a microstructure with vertical sidewall is to be fabricated using wet anisotropic etching. In most commonly employed etchants (i.e. TMAH and KOH), potassium hydroxide (KOH) exhibits higher etch rate and provides improved a...
متن کاملAnisotropic multi-step etching for large-area fabrication of surface microstructures on stainless steel to control thermal radiation
Controlling the thermal radiation spectra of materials is one of the promising ways to advance energy system efficiency. It is well known that the thermal radiation spectrum can be controlled through the introduction of periodic surface microstructures. Herein, a method for the large-area fabrication of periodic microstructures based on multi-step wet etching is described. The method consists o...
متن کاملNondestructive nanofabrication on Si(100) surface by tribochemistry-induced selective etching
A tribochemistry-induced selective etching approach is proposed for the first time to produce silicon nanostructures without lattice damage. With a ~1 nm thick SiOx film as etching mask grown on Si(100) surface (Si(100)/SiOx) by wet-oxidation technique, nano-trenches can be produced through the removal of local SiOx mask by a SiO2 tip in humid air and the post-etching of the exposed Si in potas...
متن کاملIntegration of Benzocyclobutene Poymers and Silicon Micromachned Structures Fabricated with Anisotropic Wet Etching
Title of thesis: INTEGRATION OF BENZOCYCLOBUTENE POYMERS AND SILICON MICROMACHNED STRUCTURES FABRICATED WITH ANISOTROPIC WET ETCHING Nima Ghalichechian, Master of Science, 2005 Thesis directed by: Professor Reza Ghodssi Department of Electrical and Computer Engineering Integration of low dielectric constant Benzocyclobutene (BCB) film with deep etched structures in silicon allows the fabricatio...
متن کاملA comprehensive review on convex and concave corners in silicon bulk micromachining based on anisotropic wet chemical etching
Wet anisotropic etching based silicon micromachining is an important technique to fabricate freestanding (e.g. cantilever) and fixed (e.g. cavity) structures on different orientation silicon wafers for various applications in microelectromechanical systems (MEMS). {111} planes are the slowest etch rate plane in all kinds of anisotropic etchants and therefore, a prolonged etching always leads to...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Micromachines
دوره 7 شماره
صفحات -
تاریخ انتشار 2016