A Novel, Layered Phase in Ti#x02010;Rich SrTiO<sub>3</sub> Epitaxial Thin Films
نویسندگان
چکیده
S. Lee, Dr. A. R. Damodaran, Dr. Z. Chen, Prof. L. W. Martin Department of Materials Science and Engineering University of California Berkeley, Berkeley , California 94720 , USA E-mail: [email protected] Dr. P. Gorai, N. Ferdous, Prof. E. Ertekin Department of Mechanical Science and Engineering University of Illinois Urbana-Champaign, Urbana , Illinois 61801 , USA N. Oh, Dr. J.-H. Kwon, Dr. A. Shah, Dr. E. Breckenfeld, Dr. R. V. K. Mangalam, Prof. P. V. Braun, Prof. M. Shim, Prof. J.-M. Zuo Department of Materials Science and Engineering and Materials Research Laboratory University of Illinois Urbana-Champaign, Urbana , Illinois 61801 , USA Dr. J. A. Moyer, Prof. P. Schiffer Department of Physics University of Illinois Urbana-Champaign, Urbana , Illinois 61801 , USA
منابع مشابه
Preparation of epitaxial PbTiO 3 thin films by metalorganic vapor phase epitaxy under reduced pressure
In this study PbTiO 3 thin films were deposited using metalorganic vapor phase epitaxy (MOVPE). Titanium-isopropoxide and tetraethyl-lead were used as the Ti and Pb precursors, and 0 2 was the oxidizing gas. A wide range of conditions for preparing high quality PbTiO 3 thin film were investigated. The epitaxial PbTiO 3 thin films were grown on (001) SrTiO 3 substrates at a growth temperature of...
متن کاملSynthesis, Characterization, and Application of Zr,Ce-TiO2/SiO2 Nanocomposite Thin Film as Visible-light Active Photocatalyst
A novel Zr,Ce-TiO2/SiO2 nanocomposite thin film was successfully prepared with various amounts of Zr4+ and Ce4+ as codopant ions for self-cleaning applications. A thin film was coated on a tile substrate by dip-coating and porous Zr,Ce-TiO2/SiO2 was obtained after heat treatment for 2 hours at 500 °C. The SEM images an...
متن کاملInterface structure and thermal stability of epitaxial SrTiO 3 thin films on
We have used medium energy ion scattering, temperature programmed desorption, and atomic force microscopy to study the interface composition and thermal stability of epitaxial strontium titanate thin films grown by molecular-beam epitaxy on Si 001 . The composition of the interface between the film and the substrate was found to be very sensitive to the recrystallization temperature used during...
متن کاملIn situ investigation of the early stage of TiO2 epitaxy on (001) SrTiO3.
We report on a systematic study of the growth of epitaxial TiO(2) films deposited by pulsed laser deposition on Ti-terminated SrTiO(3) (001) single crystals. By using in situ reflection high energy electron diffraction, low energy electron diffraction, x-ray photoemission spectroscopy, and scanning probe microscopy, we show that the stabilization of the anatase (001) phase is preceded by the gr...
متن کاملTerahertz spectroscopy studies on epitaxial vanadium dioxide thin films across the metal-insulator transition.
We present results on terahertz (THz) spectroscopy on epitaxial vanadium dioxide (VO(2)) films grown on sapphire across the metal-insulator transition. X-ray diffraction indicates the VO(2) film is highly oriented with the crystallographic relationship: (002)(film)//(0006)(sub) and [010](film)//[2 ̅1 ̅10](sub). THz studies measuring the change in transmission as a function of temperature demonstr...