The Fabrication of Micro-Array Channels with the Ultrafine-Grained LZ91 Mg-Li Alloy by Micro-Embossing
نویسندگان
چکیده
The fabrication of the micro-channel array through micro-embossing on an ultrafine-grained (UFG) LZ91 Mg-Li alloy was investigated in this paper. Micro-embossing tests indicated that the depth of the channels increase with increasing temperatures. Micro-array channels with widths ranging from 50 μm to 200 μm were performed with an applied force of 2 kN at 423 K, following by a dwell time of 60 s on the UFG LZ91 Mg-Li alloy. The surface topography indicates that embossed micro-channels for UFG LZ91 Mg-Li with all widths are clearly printed well with good geometrical transferability and no obvious defects. The comparison filling behavior of UFG and the CG LZ91 Mg-Li alloy reveals that grain sizes mainly affect the filling quality of micro-embossing. The results indicate a potential application of the UFG Mg-Li alloy in the mass fabrication of micro-electro-mechanical system (MEMS) components.
منابع مشابه
Dynamic Micro-strain Analysis of Ultrafine-grained Aluminum Magnesium alloy using Digital Image Correlation
Tensile tests were performed in situ on an ultrafine-grained (UFG) Al-Mg alloy using a micro-tensile module in a scanning electron microscope (SEM). The micro-strain evolution was tracked and measured using digital image correlation (DIC). A fine random speckle pattern was required to achieve high resolution and accuracy of strain measurement using DIC. To produce the speckle pattern, a pattern...
متن کاملDeveloping ultrafine-grained materials with high strength and good ductility for micro-forming applications
Materials with ultrafine grain sizes are attractive for use in micro-forming operations. High-pressure torsion (HPT) is an effective technique that allows disc materials subjected to torsional deformation to generate microstructures with significant grain refinement. Generally, ultrafine-grained materials exhibit high strength but their ductility is limited because they have both a low rate of ...
متن کاملFabrication of Al/Graphite/Al2O3 Surface Hybrid Nano Composite by Friction Stir Processing and Investigating The Wear and Microstructural Properties of The Composite
Friction stir processing was applied for fabricating an aluminum alloy based hybrid nano composite reinforced with nano sized Al2O3 and micro sized graphite particles. A mixture of Al2O3 and graphite particles was packed into a groove with 1 mm width and 4.5 mm depth, which had been cut in 5083 aluminum plate of 10 mm thick. Packed groove was subjected to friction stir processing in order to im...
متن کاملMicrostructural Evolution at Micro/Meso-Scale in an Ultrafine-Grained Pure Aluminum Processed by Equal-Channel Angular Pressing with Subsequent Annealing Treatment
Micro-forming with ultrafine-grained (UFG) materials is a promising direction for the fabrication of micro-electro-mechanical systems (MEMS) components due to the improved formability, good surface quality, and excellent mechanical properties it provides. In this paper, micro-compression tests were performed using UFG pure aluminum processed by equal-channel angular pressing (ECAP) with subsequ...
متن کاملMicro Machining of Injection Mold Inserts for Fluidic Channel of Polymeric Biochips
Recently, the polymeric micro-fluidic biochip, often called LOC (lab-on-a-chip), has been focused as a cheap, rapid and simplified method to replace the existing biochemical laboratory works. It becomes possible to form miniaturized lab functionalities on a chip with the development of MEMS technologies. The micro-fluidic chips contain many micro-channels for the flow of sample and reagents, mi...
متن کامل