Phase Separation kinetics in Fe-Cr-Al alloy
نویسندگان
چکیده
9 The α α phase separation kinetics in a commercial Fe-20 wt% Cr-6% Al oxide dispersion-strengthened PM 1
منابع مشابه
Effect of external stress on the Fe-Cr phase separation in 15-5 PH and Fe-15Cr-5Ni alloys.
The effect on Fe-Cr phase separation of a uniaxial stress during thermal ageing at 425 °C is investigated on a Fe-15Cr-5Ni steel, a model alloy of commercial 15-5 PH steel. The applied stress is shown to accelerate the ageing kinetics, and influence the morphology of Cr rich domains. A dependence of the phase separation decomposition kinetics on the relative orientations of the load and the cry...
متن کاملEffect of surface-applied reactive elements on the early stage oxidation of Fe- 18Cr-5Al and Fe-18Cr-5Al-1Hf alloys
The effect of lanthanum implantation on the early stage oxidation of Fe-18wt%Cr5wt%Al and Fe-l8wt%Cr-5wt%Al-Iwt%Hf alloys at 1100 OC has been investigated. I t was found that the reactive element enriched surfaces oxidized almost two times faster initially, and the scale that formed had a higher iron content. An extremely wavy scale/alloy interface developed in the early stage due to the accele...
متن کاملKINETICS OF -Fe NANOCRYSTALLIZATION IN Fe55Cr18Mo7B16C4 BULK AMORPHOUS ALLOY
Abstract: In this research work, crystallization kinetics of Fe55Cr18Mo7B16C4 alloy was evaluated by X-ray diffraction, TEM observations and differential scanning calorimetric tests. In practice, crystallization and growth mechanisms were investigated using DSC tests in four different heating rates. Results showed that a two -step crystallization process occurred in the alloy in which - Fe phas...
متن کاملCharacteristics of Fe-Cr-Al Alloy Nanopowders Prepared by Electrical Wire Explosion Process under Liquid Media
Fe-Cr-Al alloy nanopowders were successfully prepared by electrical wire explosion method in ethyl alcohol media. The formation of FeCr-Al alloy nanopowder was monitored by X-ray diffraction. The alloy powders have spherical shape and nanometer size. The alloy powders prepared by the electrical wire explosion method have main crystal structures of bcc Fe-Cr alloy. The geometric mean diameter an...
متن کاملStable Quasicrystalline Phase in Al-Cu-Fe-Cr Coating Materials
Transmission electron microscopy (TEM) studies have been carried out on magnetron-sputtered coatings in the Al-rich region of the Al-Cu-Fe-Cr quasicrystalline phase field, focusing on the composition that exhibited the best tribological performance among a group of sputtered coatings. The size of the particles in the as-deposited coating is around 10 nm. The TEM experiments on annealed coatings...
متن کامل