Point defect balance in epitaxial GaSb
نویسندگان
چکیده
All material supplied via Aaltodoc is protected by copyright and other intellectual property rights, and duplication or sale of all or part of any of the repository collections is not permitted, except that material may be duplicated by you for your research use or educational purposes in electronic or print form. You must obtain permission for any other use. Electronic or print copies may not be offered, whether for sale or otherwise to anyone who is not an authorised user.
منابع مشابه
Observation of T2-like coherent optical phonons in epitaxial Ge2Sb2Te5/GaSb(001) films
The phonon spectrum of Ge₂Sb₂Te₅ is a signature of its crystallographic structure and underlies the phase transition process used in memory applications. Epitaxial materials allow coherent optical phonons to be studied in femtosecond anisotropic reflectance measurements. A dominant phonon mode with frequency of 3.4 THz has been observed in epitaxial Ge₂Sb₂Te₅ grown on GaSb(001). The dependence ...
متن کاملInvestigations into molecular beam epitaxial growth of InAs/GaSb superlattices
Approved: ____________________________________ Thesis Supervisor ____________________________________ Title and Department ____________________________________ Date 1 INVESTIGATIONS INTO MOLECULAR BEAM EPITAXIAL GROWTH OF INAS/GASB SUPERLATTICES by Lee Michael Murray A thesis submitted in partial fulfillment of the requirements for the Doctor of Philosophy degree in Physics in the Graduate Coll...
متن کاملNanoporous Structure Formation in GaSb, InSb, and Ge by Ion Beam Irradiation under Controlled Point Defect Creation Conditions
Ion beam irradiation-induced nanoporous structure formation was investigated on GaSb, InSb, and Ge surfaces via controlled point defect creation using a focused ion beam (FIB). This paper compares the nanoporous structure formation under the same extent of point defect creation while changing the accelerating voltage and ion dose. Although the same number of point defects were created in each ...
متن کاملAnalysis of Recombination Processes in 0.5-0.6 eV Epitaxial GaInAsSb Lattice-matched to GaSb
This work sununanzes recent data on minority carrier lifetime in nand p-type double heterostructures (DHs) of 0.5-0.6 eV GalnAsSb confined with GaSb and AIGaAsSb cap layers. Recombination times were measured by time-resolved photoluminescence (TRPL) and by optical frequency response (OFR) to sinusoidal excitation. It was shown that one of the mechanisms responsible for interface recombination i...
متن کاملPhase separation and defect formation in stable, metastable, and unstable GaInSaSb alloys for infrared applications
GaInAsSb is a promising material for mid-infrared devices such as lasers and detectors because it is a direct band gap material with large radiative coefficient and a cut-off wavelength that can be varied across the mid-infrared (from 1.7 to 4.9 μm) while remaining lattice matched to GaSb. On the other hand, the potential of the alloy is hampered by predicted ranges of concentration where the c...