Effects of etching and adhesive applications on the bond strength between composite resin and glass-ionomer cements
نویسندگان
چکیده
OBJECTIVE This study determined the effects of various surface treatment modalities on the bond strength of composite resins to glass-ionomer cements. MATERIAL AND METHODS Conventional (Ketac Molar Quick Applicap) or resin-modified (Photac Fil Quick Aplicap) glass-ionomer cements were prepared. Two-step etch-rinse & bond adhesive (Adper Single Bond 2) or single-step self-etching adhesive (Adper Prompt L-Pop) was applied to the set cements. In the etch-rinse & bond group, the sample surfaces were pre-treated as follows: (1) no etching, (2) 15 s of etching with 35% phosphoric acid, (3) 30 s of etching, and (4) 60 s of etching. Following the placement of the composite resin (Filtek Z250), the bond strength was measured in a universal testing machine and the data obtained were analyzed with the two-way analysis of variance (ANOVA) followed by the Tukey's HSD post hoc analysis (p=0.05). Then, the fractured surfaces were examined by scanning electron microscopy. RESULTS The bond strength of the composite resin to the conventional glass-ionomer cement was significantly lower than that to the resin-modified glass-ionomer cement (p<0.001). No significant differences were determined between the self-etching and etch-rinse & bond adhesives at any etching time (p>0.05). However, a greater bond strength was obtained with 30 s of phosphoric acid application. CONCLUSIONS The resin-modified glass-ionomer cement improved the bond strength of the composite resin to the glass-ionomer cement. Both etch-rinse & bond and self-etching adhesives may be used effectively in the lamination of glass-ionomer cements. However, an etching time of at least 30 s appears to be optimal.
منابع مشابه
Shear bond strength evaluation of resin composite to resin-modified glass-ionomer cement using three different resin adhesives vs. glass-ionomer based adhesive
Background: The clinical success of sandwich technique depends on the strength of resin-modified glass ionomer cement (RMGIC) bonding to both dentin and resin composite. Therefore, the shear bond strength (SBS) of resin composite bonded to RMGIC utilizing different resin adhesives versus a GIC-based adhesive was compared. Materials and methods: In this in vitro study, 84 holes (5×2 mm) were pre...
متن کاملEffect of Self-etching Adhesives on the Bond Strength of Glass-Ionomer Cements
OBJECTIVE STATEMENT OF PROBLEM Adequate bond strength between glass ionomer cements and composite resin is necessary for the success of the sandwich technique. PURPOSE OF STUDY This study assessed the micro-shear bond strength of composite resin to glass-ionomer cements (GIC) using self-etch adhesives with different pH values. MATERIALS AND METHODS One hundred specimens (6×4×2 mm) were m...
متن کاملبررسی اثرکامپوزیت Light Cure و کامپوزیت Self Cure بر باندگلاس آینومر نوری به عاج دندان (In-vitro)
Statement of Problem: Composite reins have recently become popular for posterior teeth restorations. Gap formation and subsequent microleakage are of the complications resulting from such restorations. One of the techniques to overcome polymerization shrinkage of composite resins is sandwich technique (application of glass ionomer as a base beneath the composite resin). Since polymerization pat...
متن کاملEffect of Incorporation of Nano-Hydroxyapatite and Nano-Zinc Oxide in Resin Modified Glass Ionomer Cement on Metal Bracket Debonding
Background and Aim: Use of fluoride releasing materials to decrease the risk of demine-ralization around orthodontic brackets would be reasonable as an adhesive for bracket bonding only if they provide acceptable shear bond strength (SBS). The aim of this study was to evaluate the SBS of resin-modified glass ionomer cements (RMGICs) modified by nano-zinc oxide (NZnO) and nano- hydroxyapatite (N...
متن کامل