Transparent free-standing film of 1-D rutile/anatase TiO2 nanorod arrays by a one-step hydrothermal process.
نویسندگان
چکیده
Through the addition of a solid-state precursor, a large-scale, transparent, and free-standing film of 1-D rutile/anatase TiO2 nanorod arrays can be fabricated by dynamically changing the acidity and concentrations of titanium and chloride ions, and creating anatase growth-friendly conditions.
منابع مشابه
نانومیله‌های نانوبرگ‌دار شده دی‌اکسید تیتانیم دوفازی به‌منظور استفاده در کاربردهای فتوالکتروشیمیایی
Rutile-phase titanium dioxide nanorod arrays were prepared by the hydrothermal method. Then, anatase-phase nanoleaves were successfully synthesized on the nanorod arrays via mild aqueous chemistry. Nanorod arrays scanning electron microscopy revealed that the thin film is uniform and crack free and the average diameter and height of the nanorods are 90 nm and 2 µm, respectively. Furthermo...
متن کاملSubstrate-free, large-scale, free-standing and two-side oriented single crystal TiO2 nanorod array films with photocatalytic properties.
A substrate-free, large-scale, free-standing and two-side oriented single crystal rutile TiO(2) nanorod array film with a thickness of over ten micrometers, self-assembled via a facile hydrothermal reaction of titanium powder in a mixture solution of H(2)O(2) and HCl, exhibits high activity for the photocatalytic degradation of methyl orange.
متن کاملDensely aligned rutile TiO2 nanorod arrays with high surface area for efficient dye-sensitized solar cells.
One-dimensional (1-D) TiO(2) nanorod arrays (NRAs) with large inner surface area are desired in dye-sensitized solar cells (DSSCs). So far, good performance of DSSCs based on 1-D rutile TiO(2) NRAs remains a challenge mainly owing to their low dye-loading ability resulting from the insufficient specific surface area of 1-D TiO(2) nanostructures. In this paper, densely aligned TiO(2) NRAs with t...
متن کاملRutile TiO2 nano-branched arrays on FTO for dye-sensitized solar cells.
Hierarchical TiO(2) nanostructures would be desirable for preparing dye-sensitized solar cells because of their large amount of dye adsorption and superior light harvesting efficiency, as well as efficient charge separation and transport properties. In this study, rutile TiO(2) nano-branched arrays grown directly on transparent conductive glass (FTO) were prepared by a facile two-step wet chemi...
متن کاملHydrothermal Etching Treatment to Rutile TiO2 Nanorod Arrays for Improving the Efficiency of CdS-Sensitized TiO2 Solar Cells.
Highly ordered TiO2 nanorod arrays (NRAs) were directly grown on an F:SnO2 (FTO) substrate without any seed layer by hydrothermal route. For a larger surface area, the second-step hydrothermal treatment in hydrochloric acid was carried out to the as-prepared TiO2 NRAs. The results showed that the center portion of the TiO2 nanorods were dissolved in the etching solution to form a nanocave at th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 51 29 شماره
صفحات -
تاریخ انتشار 2015