X-ray photoelectron spectroscopy of CeO2–Na2O–SiO2 glasses

A series of (CeO2)x–(Na2O)0.3–(SiO2)(0.7−x) glasses, where 0.025≤ x≤ 0.075, have been synthesized and investigated by mean of X-ray photoelectron spectroscopy (XPS). The Ce 3d spin-orbit doublet was curve fitted in order to quantify the proportions of each cerium oxidation state in these glasses. It was found that Ce ions are predominantly in the Ce(III) state in glasses with compositions x≤ 0.075, while mixed Ce valences were found in the glass with composition x= 0.10. The O 1s spectra have also been curve fitted with two components, one from bridging oxygen (BO) and the other from non-bridging oxygen atoms (NBO). The measured number of NBO, based on the fact that only oxygen atoms in the site Si–O–Na+ contribute to the NBO peak, was found to be constant at ∼35% for all samples, in good agreement with t i ©