In Vitro Biocompatibility of Si Alloyed Multi-Principal Element Carbide Coatings
نویسندگان
چکیده
In the current study, we have examined the possibility to improve the biocompatibility of the (TiZrNbTaHf)C through replacement of either Ti or Ta by Si. The coatings were deposited on Si and 316L stainless steel substrates by magnetron sputtering in an Ar+CH4 mixed atmosphere and were examined for elemental composition, chemical bonds, surface topography, surface electrical charge and biocompatible characteristics. The net surface charge was evaluated at nano and macroscopic scale by measuring the electrical potential and work function, respectively. The biocompatible tests comprised determination of cell viability and cell attachment to the coated surface. The deposited coatings had C/(metal+Si) ratios close to unity, while a mixture of metallic carbide, free-carbon and oxidized species formed on the film surface. The coatings' surfaces were smooth and no influence of surface roughness on electrical charge or biocompatibility was found. The biocompatible characteristics correlated well with the electrical potential/work function, suggesting a significant role of surface charge in improving biocompatibility, particularly cell attachment to coating's surface. Replacement of either Ti or Ta by Si in the (TiZrNbTaHf)C coating led to an enhanced surface electrical charge, as well as to superior biocompatible properties, with best results for the (TiZrNbSiHf)C coating.
منابع مشابه
ارزیابی مقاومت به اکسایش پیوسته پوشش پاشش حرارتی Mo-Si-B روی فولاد ساده کربنی
In this study, Mo-14Si-10B and Mo-57Si-10B (at%) elemental powders were separately milled using an attritor mill. Mechanically alloyed powders were agglomerated and annealed. Then, powders of Mo-Si-B as alloyed (with composites) and agglomerated (without composites) were plasma sprayed onto plain carbon steels. The samples, both coated and non-coated, were subjected to isothermal oxidation test...
متن کاملProperties of titanium-alloyed DLC layers for medical applications
DLC-type layers offer a good potential for application in medicine, due to their excellent tribological properties, chemical resistance, and bio-inert character. The presented study has verified the possibility of alloying DLC layers with titanium, with coatings containing three levels of titanium concentration prepared. Titanium was present on the surface mainly in the form of oxides. Its incr...
متن کاملSLURRY EROSION RESISTANCE OF LASER CLAD Fe–Cr–B–Si COATINGS
The slurry erosion behaviour of laser clad Fe–Cr–B–Si alloy coatings was investigated at impact angles from 30u to 90u with an increment of 15u, and compared with the slurry erosion behaviour of two laser clad carbide coatings and a non-coated substrate made of AISI 4140 steel. The Fe–Cr–B–Si alloy coatings had slurry erosion resistance. Their overall slurry erosion resistance at impact angles ...
متن کاملارزیابی فازی ترکیبات آلیاژی و کامپوزیتی شده ی دی سیلیساید مولیبدن با آلومینیوم و کاربید تیتانیوم
In this study, pure powders such as molybdenum, silicon, aluminum and titanium carbide were utilized to produce MoSi2 compound, MoSi2 /20 Vol % TiC composite, MoSi2-x Al alloyed compound and MoSi2-x Al/20 Vol % TiC alloyed composite. The initial powders were mixed in specified ratios, and then, were activated by mechanical milling. Milled powders were compacted, synthesized and sintered in the...
متن کاملSimilarities and Differences in Mechanical Alloying Processes of V-Si-B and Mo-Si-B Powders
V-Si-B and Mo-Si-B alloys are currently the focus of materials research due to their excellent high temperature capabilities. To optimize the mechanical alloying (MA) process for these materials, we compare microstructures, morphology and particles size as well as hardness evolution during the milling process for the model alloys V-9Si-13B and Mo-9Si-8B. A variation of the rotational speed of t...
متن کامل