Influence of Ceramic Technology on the Microstructure and Ferroelectric Properties of Transparent Plzt Ceramics
نویسندگان
چکیده
Mixed-oxides and the coprecipitation procedure were used to prepare PLZT x/65/35 powders. Transparent samples were obtained by hot-pressing. The influence of processing parameters on the microstructure and electrical properties was studied.
منابع مشابه
DIELECTRIC , FERROELECTRIC AND PIEZOELECTRIC PROPERTIES OF La 3 + SUBSTIUTED PZT CERAMICS
Lanthanum substituted lead zirconate titanate (PLZT) nanocrystallite with stichometry formula Pb0.90La0.10 (Zr0.52Ti0.48) O3 have been synthesized by sol gel process. The effect of nanocrystallite on dielectric, ferroelectric and piezoelectric properties of La substituted PZT was studied. The average crystallite size of the PLZT powder was 21nm.Variation of dielectric constant with temperature ...
متن کاملStudying the Effects of Nano Sintering Additives on Microstructure and Electrical Properties of Potassium-Sodium Niobate Piezoceramics
In this paper, lead free (K0.48,Na0.52)NbO3 (KNN(48-52)) piezoelectric ceramics were made by conventional solid state sintering process. Additives of nano ZnO (n-ZnO), nano CuO (n-CuO) and nano SnO2 (n-SnO2) were used in order to decrease the sintering temperature, as well as modifying the dielectric, piezoelectric and ferroelectric propert...
متن کاملInvestigation the Effect of Niobium Oxide Additive on the Dielectric Properties of Bismuth Titanate
Bismuth titanate ceramic has been attracted as a lead-free ferroelectric due to its high Curie temperature in high temperature applications as well as high frequency applications. In this study, the effect of niobium oxide as an additive on the microstructure and dielectric properties of bismuth titanate ceramic was investigated. For this purpose, niobium oxide was added to bismuth titanate, sy...
متن کاملPreparation and characterization of transparent PZN–PLZT ceramics
Transparent Pb(Zn1/3Nb2/3)O3–(Pb1-xLax)(Zr1-yTiy)O3 (PZN–PLZT) ferroelectric ceramics have successfully been prepared by hot-pressed sintering in oxygen atmosphere. Uniform cylindrical samples with diameter as large as 50 mm can readily be obtained. X-ray analysis and scanning electron microscopy experiments showed a pure perovskite phase, thin grain boundaries, and uniform dense microstructure...
متن کاملGelcasting as a Novel Processing Route to Fabricate Partially Stabilized Zirconia Ceramic Bodies
Bioinert ceramics, like alumina and zirconia are used mainly for replacements of bones, hip joints and for dental implants. Partially stabilized zirconia ceramics (PSZ or TZP with 3 mol.% or 5 wt.% Y2O3), appear as perspective bioinert ceramics because of their high strength and corrosion resistance. In order to fabricate complex shapes, it is essential to use a near ...