Sintering Effects on Mechanical Properties of Dentine Derived Hydroxyapatite-glass Composites
نویسندگان
چکیده
DENTINE DERIVED HYDROXYAPATITE-GLASS COMPOSITES L.S. Ozyegin, F.N. Oktar, U. Karacayli, C. Aktas, S. Agathopoulos, C. Kalkandelen, M. Yetmez Marmara University, Istanbul, Turkey; Gulhane Military Medical Academy, Ankara, Turkey; Leibniz Institute for New Materials, Saarbrücken, Germany; Ioannina University, Ioannina, Greece; Istanbul University, Istanbul, Turkey; Bulent Ecevit University, Zonguldak, Turkey
منابع مشابه
An investigation on Mechanical Properties of Apatite-Wollastonite-Diopside Glass-Ceramics Composites
Apatite-wollastonite (A-W)-phlogopite glass-ceramic is considered to be difficult to resorb, but often, it has been incorporated in particulate form to create new bioactive composites for potential maxillofacial applications. With various compositions, the present work has attempted to prepare apatite-wollastonite (A-W)-phlogopite glass ceramic composites, by applying sintering. Here, three-poi...
متن کاملBiocompatibility of Hydroxyapatite-Alumina and Hydroxyapatite-Zirconia Composites including Commercial Inert Glass (CIG) as a Ternary Component
Hydroxyapatite (HA), chemical formula Ca10(PO4)6(OH)2, is a very popular bioceramic for orthopedic and dental applications. Although HA has excellent biocompatibility, its inferior mechanical properties make it unsuitable for load-bearing implant applications. Therefore,HA should be strengthened by a secondary phase to produce a composite that possesses robust mechanical properties. The aim of ...
متن کاملMechanical properties of bovine hydroxyapatite (BHA) composites doped with SiO2, MgO, Al2O3, and ZrO2.
Biologically derived hydroxyapatite from calcinated (at 850 degrees C) bovine bones (BHA) was doped with 5 wt% and 10 wt% of SiO(2), MgO, Al(2)O(3) and ZrO(2) (stabilized with 8% Y(2)O(3)). The aim was to improve the sintering ability and the mechanical properties (compression strength and hardness) of the resultant BHA-composites. Cylindrical samples were sintered at several temperatures betwe...
متن کاملReaction Sintering and Mechanical Properties of Hydroxyapatite–Zirconia Composites with Calcium Fluoride Additions
The effects of calcium fluoride (CaF2) additions on the densification and mechanical properties of hydroxyapatite–zirconia composites (HA–ZrO2) were investigated. When small amount of CaF2 was added, the density of the composites was markedly enhanced. The reactions of HA with CaF2, which led to the formation of fluorapatite (FA), were attributed to the observed improvements in densification. W...
متن کاملGlass-reinforced hydroxyapatite composites: secondary phase proportions and densification effects on biaxial bending strength.
CaO-P(2)O(5) glasses with additions of MgO and CaF(2) were used as a sintering aid of hydroxyapatite, and glass-reinforced hydroxyapatite composites obtained. Glasses promoted significant changes in the microstructure of the composites, namely with the formation of tricalcium phosphate secondary phases, beta and alpha-TCP. Quantitative phase analysis was performed by the Rietveld method using G...