Deformation behavior of duplex austenite and ε-martensite high-Mn steel
نویسندگان
چکیده
Deformation and work hardening behavior of Fe-17Mn-0.02C steel containing ε-martensite within the austenite matrix have been investigated by means of in situ microstructural observations and x-ray diffraction analysis. During deformation, the steel shows the deformation-induced transformation of austenite → ε-martensite → α'-martensite as well as the direct transformation of austenite → α'-martensite. Based on the calculation of changes in the fraction of each constituent phase, we found that the phase transformation of austenite → ε-martensite is more effective in work hardening than that of ε-martensite → α'-martensite. Moreover, reverse transformation of ε-martensite → austenite has also been observed during deformation. It originates from the formation of stacking faults within the deformed ε-martensite, resulting in the formation of 6H-long periodic ordered structure.
منابع مشابه
The Effect of Nitrogen on Martensite Formation in a Cr-Mn-Ni Stainless Steel
The influence of nitrogen (0 to 0.27 wtYo) on martensite formation in an experimental low-nickel stainless-steel alloy (Fe-17Cr-7Mn-4Ni) has been investigated. The alloys containing 0.1 wtYo or more nitrogen are fully austenitic at room temperature; those containing less nitrogen consist of a mixture of austenite, martensite and S-ferrite. The alloys containing less than 0.2 wtYo nitrogen are m...
متن کاملStacking Fault Energy and Microstructural Insight into the Dynamic Deformation of High-Manganese TRIP and TWIP Steels
The dynamic behavior of three high manganese steels with very different stacking faultenergy (SFE) values (4-30 mJ/m2) were studied using high strain rate torsional tests. The hotrolledmicrostructure of the steel with the lowest SFE of 4 mJ/m2 consisted of a duplex mixture ofaustenite and ε-martensite, but those of the other two steels were fully austenitic. The deformedmicrostructures were stu...
متن کاملMicrostructure and Tensile-Shear Properties of Resistance Spot-Welded Medium Mn Steel
The medium Mn steels are gaining increasing attention due to their excellent combination of mechanical properties and material cost. A cold-rolled 0.1C5Mn medium Mn steel with a ferrite matrix plus metastable austenite duplex microstructure was resistance spot-welded with various welding currents and times. The nugget size rose with the increase of heat input, but when the welding current excee...
متن کاملDevelopment of Ultrafine Lamellar Ferrite and Austenite Duplex Structure in 0.2C5Mn Steel during ART-annealing
The microstructural evolution of Fe–0.2C–5Mn steel during intercritical annealing with holding time for up to 144 hours was examined by TEM and STEM. It was demonstrated by TEM that the martensite lath structure gradually transformed into a lamellar ferrite and austenite duplex structure. The partitioning of manganese from ferrite to austenite was found by STEM. Typical Kurdjumov-Sachs orientat...
متن کاملInfluence of Initial Microstructure on Hot Deformation Behavior of Duplex Stainless Steels
In this research the effect of initial microstructure on hot deformation behavior in terms of Ferrite-to-Austenite ratios is studied. Two types of stainless steels C1 and C2 were homogenizing heat-treated and deformed under hot compression examinations at temperatures 900ºC and 1100ºC at strain rate of 0.1s-1. The results showed that the flow stress levels of specimens are strongly r...
متن کامل