Single-crystalline LaB6 nanowires.
نویسندگان
چکیده
Lanthanum hexaboride nanowires produced by chemical vapor deposition are single-crystalline and grown along the [111] direction. Streaks appearing in the electron diffraction spots indicate the lateral direction perpendicular to the nanowire growth axis.
منابع مشابه
Hydrothermal synthesis and magnetic properties of single-crystalline BiFeO3 nanowires.
One-dimensional, single-crystalline BiFeO(3) nanowires presenting a diameter of 45-200 nm and a length from hundreds of nanometres to several microns have been prepared using an improved hydrothermal method. The characterization results of ZFC and FC magnetizations at different temperatures indicate that single-crystalline BiFeO(3) nanowires show a spin-glass transition below the freezing tempe...
متن کاملOne-dimensional single-crystalline Mn3O4 nanostructures with tunable length and magnetic properties of Mn3O4 nanowires.
A facile, solution-phase route to mass fabrication of one-dimensional single crystalline Mn(3)O(4) nanowires with a unique core/sheath heteronanostructure, controlled aspect ratios, and narrow diameter distribution was reported. The single crystalline Mn(3)O(4) nanowires have considerably large coercivities (H(C) > 1 T) at low temperatures.
متن کاملSingle-Crystalline Mesoporous Molybdenum Nitride Nanowires with Improved Electrochemical Properties
We report single-crystalline mesoporous molybdenum nitride nanowires (meso-Mo3N2-NWs) prepared by topotactic reaction using single-crystalline molybdenum oxide nanowires. The single-crystalline nature of meso-Mo3N2-NWs was clearly observed by field-emission transmission electron microscopy. The meso-Mo3N2-NWs exhibited mesoporous structure with 45 m/g in specific surface area and 4.6 nm in aver...
متن کاملPulsed laser deposition of single-crystalline Cu7In3/CuIn0.8Ga0.2Se2 core/shell nanowires
UNLABELLED Single-crystalline Cu7In3/CuIn0.8Ga0.2Se2 (CI/CIGS) core/shell nanowires are fabricated by pulsed laser deposition with Ni nanoparticles as catalyst. The CI/CIGS core/shell nanowires are made up of single-crystalline CI cores surrounded by single-crystalline CIGS shells. The CI/CIGS nanowires are grown at a considerably low temperature (350°C ~ 450°C) by vapor-liquid-solid mode combi...
متن کاملSingle-crystalline vanadium dioxide nanowires with rectangular cross sections.
We report the synthesis of single-crystalline VO2 nanowires with rectangular cross sections using a vapor transport method. These nanowires have typical diameters of 60 (+/-30) nm and lengths up to >10 mum. Electron microscopy and diffraction measurements show that the VO2 nanowires are single crystalline and exhibit a monoclinic structure. Moreover, they preferentially grow along the [100] dir...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Journal of the American Chemical Society
دوره 127 9 شماره
صفحات -
تاریخ انتشار 2005