Characterization and Performance of LiFePO4 Thin-Film Cathodes Prepared with Radio-Frequency Magnetron-Sputter Deposition
نویسندگان
چکیده
Characterization and Performance of LiFePO4 Thin-Film Cathodes Prepared with Radio-Frequency Magnetron-Sputter Deposition Jian Hong,* Chunsheng Wang,** Nancy J. Dudney,** and Michael J. Lance Department of Chemical Engineering, Tennessee Technological University, Cookeville, Tennessee 38505, USA Department of Chemical and Biochemical Engineering, University of Maryland, College Park, Maryland 20742, USA Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831, USA
منابع مشابه
Reduced surface roughness of solid thin films prepared by alternating-bias, radio-frequency magnetron sputtering
Surface roughness that is associated with thin-film deposition has a direct effect on the optical, electrical, and mechanical quality of solid-thin-film devices. The effect of using alternating bias during rf-magnetron sputtering of SiO2 on Si substrate was investigated, and it was proven experimentally that modulating the plasma flow by means of alternating bias produces more even deposition o...
متن کاملSodium Manganese Oxide Thin Films as Cathodes for Na-Ion Batteries
This paper presents the fabrication and characterization of sodium manganese oxide cathode thin films for rechargeable Na-ion batteries. Layered oxide compounds of nominal compositions Na0.6MnO2 and Na1.0MnO2 have been prepared by radio frequency magnetron sputtering and post-annealing at high temperatures under various conditions. The Na0.6MnO2 thin films possess either a hexagonal or orthorho...
متن کاملDevelopment and characterization of a secondary RF plasma-assisted closed-field dual magnetron sputtering system for optical coatings on large-area substrates
An RF-assisted closed-field dual magnetron sputtering system was developed to characterize the plasma and the ionization fraction of sputtered material to provide a suitable system for depositing optical thin films on large-area substrates at low temperatures (<130 ◦C). The ‘prototype’ system consists of dual 76 mm dc magnetrons operated at both balanced and unbalanced (closed-field) configurat...
متن کاملCharacteristics of ZnO thin films prepared by radio frequency magnetron sputtering
We investigated in this study structural and nanomechanical properties of zinc oxide (ZnO) thin films deposited onto Langasite substrates at 200 C through radio frequency magnetron sputtering with an radio frequency power at 200 W in an O2/Ar gas mixture for different deposition time at 1, 2, and 3 h. Surface morphologies and crystalline structural characteristics were examined using X-ray diff...
متن کاملCharacterization and Microstructure of Titanium Dioxide Prepared by Radio Frequency Magnetron Sputtering
Titanium oxide (TiO2) thin films were deposited by RF magnetron sputtering on Si and glass substrates. The microstructure, surface morphology, and optical properties of the thin films were investigated by grazing incidence X-ray diffraction (GIXD), transmission electron microscopy (TEM), field emission scanning electron microscopy (FE-SEM), atomic force microscopy (AFM), and UV/VIS spectrophoto...
متن کامل