Semiconductors crystal facet engineering has become an important strategy for properly tuning and optimizing both the physicochemical properties and the reactivity of photocatalysts. In this review, a concise survey of recent results obtained in the field of specific surface-oriented anatase TiO2 crystals preparation is presented. The attention is mainly focused on the fluorine-mediated hydrothermal and/or solvothermal processes employed for the synthesis and the assembly of anatase micro/nanostructures with dominant {001} facets. Their peculiar photocatalytic properties and potential applications are also presented, with a particular focus on photocatalysis-based environmental clean up and solar energy conversion applications. Finally, the most promising results obtained in the engineering of TiO2 anatase crystal facets obtained by employing alternative, possibly more environmentally friendly methods are critically compared.
منابع مشابه
Synthesis of nano-sized anatase TiO2 with reactive {001} facets using lamellar protonated titanate as precursor.
Nano-sized anatase TiO(2) with exposed {001} facets was synthesized from lamellar protonated titanate precursor. Owing to small size (ca. 11 nm) and high surface area (155 m(2) g(-1)), the crystals with 26.1% {001} facets exhibited markedly superior photoactivity to reference ca. 76 nm anatase TiO(2) nanosheets with 88.4% {001} facets.
متن کاملAnatase TiO2 crystals with exposed high-index facets.
Put your best face forward: The performance of TiO2 anatase crystals in energy and environmental applications is normally correlated with the TiO2 crystal facets exposed, and increasing the percentage of highly reactive surfaces is extremely important. A new gas-phase oxidation process using TiCl4 as precursor now yields anatase TiO2 single crystals with primarily high-index {105} facets, which...
متن کاملThe synthesis of nitrogen/sulfur co-doped TiO2 nanocrystals with a high specific surface area and a high percentage of {001} facets and their enhanced visible-light photocatalytic performance
Nitrogen/sulfur co-doped anatase TiO2 nanocrystals with a high specific surface area and a high percentage of {001} facets were synthesized by a solvent-thermal process followed by the calcination with thiourea at an optimum heat treatment temperature. Under current experimental conditions, the optimum heat treatment temperature was found at 300°C, which successfully introduced nitrogen and sul...
متن کاملTuning TiO2 nanoparticle morphology in graphene-TiO2 hybrids by graphene surface modification.
We report the hydrothermal synthesis of graphene (GNP)-TiO2 nanoparticle (NP) hybrids using COOH and NH2 functionalized GNP as a shape controller. Anatase was the only TiO2 crystalline phase nucleated on the functionalized GNP, whereas traces of rutile were detected on unfunctionalized GNP. X-Ray Photoelectron spectroscopy (XPS) showed C-Ti bonds on all hybrids, thus confirming heterogeneous nu...
متن کاملUpgrading TiO2 Photoactivity under Visible Light by Synthesis of MWCNT/TiO2 Nanocomposite
Nanocomposites of multi-walled carbon nanotubes and titanium dioxide (MWCNT/TiO2) were synthesized by the sol-gel method. Regarding hydrophobicity of carbon nanotubes (CNTs), benzyl alcohol was used as the linking agent between CNT powder and TiO2 gel which was prepared from the precursor of titanium tetraisopropoxide. The prepared samples were treated under thermal treatments. A part of the sa...