Observation of pH-, solvent-, spin-, and excitation-dependent blue photoluminescence from carbon nanoparticles.
نویسندگان
چکیده
Highly blue luminescent carbon nanoparticles with photo-luminescence quantum yields of 31.6%-40.6% were prepared by a one-step pyrolytic route from ethylenediamine-tetraacetic acid salts and a unique emission that is strongly dependent on pH, solvent, spin, and excitation wavelength was observed.
منابع مشابه
Observation of strong direct-like oscillator strength in the photoluminescence of Si nanoparticles
We have performed time-resolved photoluminescence measurements on suspensions of silicon nanoparticles using near-infrared two-photon femtosecond excitation. Our results for 1 nm particles show wide bandwidth but indicate full conversion to directlike behavior, with a few nanosecond time characteristic, corresponding to oscillator strength comparable to those in direct semiconductors. In additi...
متن کاملHigh-Efficient Excitation-Independent Blue Luminescent Carbon Dots
Blue luminescent carbon dots (CDs) were synthesized by the hydrothermal method. Blue-shifts of the maximum emission wavelength from 480 to 443 nm were observed when the concentration of CD solution decreased. The photoluminescence (PL) spectra of CDs at low concentration showed an excitation-independent behaviour, which is very different from the previous reports. Two different emitting mechani...
متن کاملA study of laser-induced blue emission with nanosecond decay of silicon nanoparticles synthesized by a chemical etching method.
Silicon nanoparticles (Si NPs), exhibiting a strong visible photoluminescence (PL), have found many applications in optoelectronics devices, biomedical tags and flash memories. Chemical etching is a well-known method for synthesizing orange-luminescent, hydride-capped silicon nanoparticles (H/Si NPs). However, a blueshift in emission wavelength occurs when reducing the particle size to exciton ...
متن کاملSilicon Nanocrystals with pH-Sensitive Tunable Light Emission from Violet to Blue-Green
We fabricated a silicon nanocrystal (NC) suspension with visible, continuous, tunable light emission with pH sensitivity from violet to blue-green. Transmission electron microscopy (TEM) images and X-ray diffraction (XRD) pattern analysis exhibit the highly crystalline nanoparticles of silicon. Photoluminescence (PL) spectra and photoluminescence excitation (PLE) spectra at different pH values,...
متن کاملPropionic-Acid-Terminated Silicon Nanoparticles: Synthesis and Optical Characterization
Photoinitiated hydrosilylation was used to attach acrylic acid to the surface of photoluminescent silicon nanoparticles, thereby producing water-dispersible, propionic-acid-terminated particles. From transmission electron microscope (TEM) observations, the average diameters of the synthesized nanocrystals were 1.9-2.4 nm. It is likely that smaller particles (<1.5 nm) were also present but could...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 46 21 شماره
صفحات -
تاریخ انتشار 2010