Effect of titanium carbide coating on the osseointegration response in vitro and in vivo.
نویسندگان
چکیده
Titanium has limitations in its clinical performance in dental and orthopaedic applications. This study describes a coating process using pulsed laser deposition (PLD) technology to produce surfaces of titanium carbide (TiC) on titanium substrates and evaluates the biological response both in vitro and in vivo. X-ray photoelectron spectroscopy (XPS) analysis revealed the presence of 18.6-21.5% TiC in the surface layer, accompanied by oxides of titanium 78.5-81.4% in the following concentrations: 11.1-13.0% Ti(2)O(3), 50.8-55.8% TiO(2), 14.5-14.7% TiO. Expression of genes central to osteoblast differentiation (alkaline phosphatase, A2 pro-collagen type 1, osteocalcin, BMP-4, TGFbeta and Cbfa-1) were up-regulated in all cell lines (primary human osteoblasts, hFOB1.19 and ROS.MER#14) grown on TiC compared with uncoated titanium when measured by semiquantitative PCR and real time-PCR, whilst genes involved in modulation of osteoclastogenesis and osteoclast activity (IL-6 and M-CSF) were unchanged. Bone density was shown to be greater around TiC-coated implants after 2 and 4 weeks in sheep and both 4 and 8 weeks in rabbits compared to uncoated titanium. Rapid bone deposition was demonstrated after only 2 weeks in the rabbit model when visualized with intravital staining. It is concluded that coating with TiC will, in comparison to uncoated titanium, improve implant hardness, biocompatibility through surface stability and osseointegration through improved bone growth.
منابع مشابه
Reality of Dental Implant Surface Modification: A Short Literature Review
Screw-shaped endosseous implants that have a turned surface of commercially pure titanium have a disadvantage of requiring a long time for osseointegration while those implants have shown long-term clinical success in single and multiple restorations. Titanium implant surfaces have been modified in various ways to improve biocompatibility and accelerate osseointegration, which results in a shor...
متن کاملExperimental determination of the carburizing effect on tensile strength, impact strength, fatigue, residual stress of nano girth welding on microalloy steel
In this article the effects of carburizing heat treatment on girth weld with containing titanium oxide and titanium carbide nanoparticles (X-65 grade of gas pipeline) is evaluated. The charpy results show that in the carburized sample containing titanium oxide and titanium carbide nanoparticles compared to the no heat treatment sample (containing titanium carbide and titanium carbide nanopartic...
متن کاملA Review on Titanium Nitride and Titanium Carbide Single and Multilayer Coatings Deposited by Plasma Assisted Chemical Vapor Deposition
In this paper, we reviewed researches about the titanium nitride (TiN) and titanium carbide (TiC) single and multilayer coatings. These coatings were deposited by the plasma assisted chemical vapor deposition (PACVD) technique. Plasma-based technologies are used for the processing of thin films and coatings for different applications such as automobile and aerospace parts, computer disc drives,...
متن کاملExperimental determination of the carburizing effect on tensile strength, impact strength, fatigue, residual stress of nano girth welding on microalloy steel
In this article the effects of carburizing heat treatment on girth weld with containing titanium oxide and titanium carbide nanoparticles (X-65 grade of gas pipeline) is evaluated. The charpy results show that in the carburized sample containing titanium oxide and titanium carbide nanoparticles compared to the no heat treatment sample (containing titanium carbide and titanium carbide nanopartic...
متن کاملIn Vitro and In Vivo Evaluation of Zinc-Modified Ca–Si-Based Ceramic Coating for Bone Implants
The host response to calcium silicate ceramic coatings is not always favorable because of their high dissolution rates, leading to high pH within the surrounding physiological environment. Recently, a zinc-incorporated calcium silicate-based ceramic Ca2ZnSi2O7 coating, developed on a Ti-6Al-4V substrate using plasma-spray technology, was found to exhibit improved chemical stability and biocompa...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Biomaterials
دوره 28 4 شماره
صفحات -
تاریخ انتشار 2007