Microleakage at the composite-repair interface: effect of different adhesive systems.

نویسندگان

  • Andrea Nóbrega Cavalcanti
  • Catarina Lavigne
  • Céres Mendonça Fontes
  • Paula Mathias
چکیده

The purpose of the present study was to evaluate the microleakage at the composite-repair interface using different bonding systems. Composite resin specimens (Filtek Z250 - 3M-ESPE) were divided into five groups (n=20) according to the following bonding mechanism: C - control - etching with 35% phosphoric acid; SB1 - etching and application of one coat of Single Bond (3M-ESPE); SB2 - etching and application of two coats of Single Bond (3M-ESPE); SMP1 - etching, application of Scotchbond Multi-Purpose primer (3M-ESPE) followed by the adhesive and, SMP2 - etching, application of Scotchbond Multi-Purpose adhesive (3M-ESPE) without the primer. Thereafter, all groups received new resin application. Samples were thermocycled (500 cycles / 5ºC - 55ºC [±2]) and immersed for 4h in 2% methylene blue buffered dye solution (7.0 pH). Three examiners measured the extent of microleakage in a stereoscope microscope, using four representative scores. For all experimental groups, no significant difference in microleakage at the repair was identified by Kruskal-Wallis test (p > 0.05). Therefore, different types of bonding systems presented the same effect on the dye penetration along the repair interface.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The effect of different concentrations of carbamide peroxide on the marginal seal of composite restorations bonded with a self-etch adhesive

Introduction: Bleaching of discolored tooth may affect the tooth/composite interface. The aim of this study was to evaluate the effect of different concentrations of carbamide peroxide (CP) on the marginal seal of composite restorations bonded with a self-etch adhesive. Materials and Methods: In this experimental study  Class V cavities were prepared on the buccal and lingual surfaces o...

متن کامل

Microleakage comparison of three types of adhesive systems versus GIC-based adhesive in class V composite restorations

Background and aims: New dentin bonding agents and techniques have been developed to reduce microleakage and create higher bond strength. This in-vitro study compared the microleakage of three resin-based adhesives versus a GIC-based adhesive on class V composite restorations.  Materials and Methods: Class V cavities were prepared on the buccal surfaces of 72 sound premolars, randomly assigned ...

متن کامل

Resin composite repair: Quantitative microleakage evaluation of resin-resin and resin-tooth interfaces with different surface treatments

OBJECTIVE The aim was to evaluate the effect of different adhesive systems and surface treatments on the integrity of resin-resin and resin-tooth interfaces after partial removal of preexisting resin composites using quantitative image analysis for microleakage testing protocol. MATERIALS AND METHODS A total of 80 human molar teeth were restored with either of the resin composites (Filtek Z25...

متن کامل

In Vitro Microleakage of Class V Composite Restorations in Use of Three Adhesive Systems

Background and Aim: Microleakage is a drawback of composite restorations and it is more noticeable in dentinal walls. Despite advances in dentin bonding agents, no adhesive can completely eliminate microleakage and provide a hermetic seal. This study aimed to compare microleakage of three resin bonding agents namely a universal adhesive, two-step self-etch system and two-step total-etch system....

متن کامل

Microleakage beneath brackets bonded with flowable materials: effect of thermocycling.

The purpose of this study was to evaluate the effects of thermocycling on microleakage beneath brackets bonded with an orthodontic composite and different flowable materials. Brackets were bonded to 200 bovine incisors divided into five groups: (1) Transbond XT, (2) X-Flow, (3) Dyract-Flow, (4) Admira-Flow, and (5) Beautiful-Flow. Half the teeth in each group were thermocycled. The specimens we...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Journal of applied oral science : revista FOB

دوره 12 3  شماره 

صفحات  -

تاریخ انتشار 2004