Growth behavior of short fatigue cracks in a SCS-6/Ti composite
نویسندگان
چکیده
The initiation and growth behavior of short fatigue cracks from the interfacial micro-notches in a SCS-6/Ti composite at various maximum applied stress levels were quantitatively characterized. Micro-notches in the interfacial reaction layer were induced by applying monotonic tensile loading prior to fatigue testing. The propagation and arrest behaviors of each individual crack were carefully monitored. An interface-controlled fatigue cracking model was used to predict several critical parameters which govern the growth behavior of fatigue cracks in the composite. © 1999 Published by Elsevier Science S.A. All rights reserved.
منابع مشابه
Short and Large Crack , Mixed - Mode Fatigue - Crack Growth Thresholds in Ti - 6 Al - 4 V
There are few experimental results to date describing the crack-propagation threshold behavior of short fatigue cracks under multiaxial loading conditions. To address this need, in the present study, the variation in mixed-mode, high-cycle fatigue-crack growth thresholds with crack size and shape are reported for a Ti-6Al-4V turbine blade alloy, heat treated to two widely different microstructu...
متن کاملMixed-Mode, High-Cycle Fatigue-Crack Growth Thresholds in Ti-6Al-4V: A Comparison of Large and Small Crack Behavior
There are few experimental results to date describing the crack-propagation threshold behavior of short fatigue cracks under multiaxial loading conditions. To address this need, in the present study, the variation in mixed-mode, high-cycle fatigue-crack growth thresholds with crack size and shape are reported for a Ti-6Al-4V turbine blade alloy, heat treated to two widely different microstructu...
متن کاملMixed-mode, high-cycle fatigue-crack growth thresholds in Ti±6Al±4V I. A comparison of large- and short-crack behavior
Mixed-mode, high-cycle fatigue-crack growth thresholds are reported for through-thickness cracks (large compared to microstructural dimensions) in a Ti±6Al±4V turbine blade alloy with a bimodal microstructure. Speci®cally, the eect of combined mode I and mode II loading, over a range of phase angles b tanÿ1 DKII=DKI from 0° to 82° DKII=DKI 0±7), is examined for load ratios (ratio of minimu...
متن کاملThe Effect of Inclusions on Through-thickness Directional Fatigue Behavior of S355N Steel Plate
Microalloyed S355N steel plates are extensively used in bridge and high-rise building structures. One of the factors affecting the mechanical properties is the size and morphology of inclusions. In this research, microalloyed S355N steel plates with different sizes of inclusions were examined. One contained long manganese sulfide inclusions (LI material) and the other had short ones (SI materia...
متن کاملShort Crack Initiation and Growth at 600oC in Notched Specimens of Inconel718
The natural initiation and growth of short cracks in Inconel 718 U-notch specimens has been studied at 600C in air. U notches were introduced through broaching, and hardness traces and optical microscopy on cross sections through the U notch broaching showed that the broaching process had introduced a deformed, work hardened layer. Fatigue tests were conducted under load control using a 1-1-1-1...
متن کامل