Plastic Deformation Influence on Intrinsic Magnetic Field of Austenitic Biomaterials
نویسندگان
چکیده
This article deals with non-destructive evaluation of austenitic stainless steels, which are used as the biomaterials in medical practice. Intrinsic magnetic field is investigated using the fluxgate sensor, after the applied plastic deformation. The three austenitic steel types are studied under the same conditions, while several values of the deformation are applied, respectively. The obtained results are presented and discussed in the paper.
منابع مشابه
The Dislocation-Enhanced Finkelshtain-Rosin Effect (DEFRE) in Austenitic Steels
A systematic study of the influence of plastic deformation and low temperature ageing on the carbon Dislocation Enhanced Finkelshtain Rosin Effect (DEFREIC) in austenitic alloys of Fe-Ni, Fe-Ni-MO, Fe-Mn-A1 and Fe-Cr-Ni systems with different carbon content is reported. The experiments prove that after plastic deformation at room temperature the FR effect is transformed into DEFREIC. nith both ...
متن کاملEffect of the Primary Microstructures during Training Producers on TWSME in NiTi Alloys (TECHNICAL NOTE)
The influence of the martensitic, martensitic+austenitic and austenitic structures in bending training on two-way shape memory effect (TWSME) in Ni-50.8 at %Ti and Ni-49.9 at %Ti alloys was studied. In addition of the primary structure, the effect of pre-strain, plastic strain, training cycle and training temperature on the TWSME was investigated. The prepared samples were trained in martensiti...
متن کاملGrain Size Effect on the Hot Deformation Processing Map of AISI 304 Austenitic Stainless Steel
In this study, the hot deformation processing map of AISI 304 austenitic stainless steel in two initial grain sizes of 15 and 40 μm was investigated. For this purpose, cylindrical samples were used in the hot compression test at the temperature range of 950-1100 °C and the strain rate of 0.005-0.5% s-1. At first, the relationship between the peak stress and Zener-Hollomon parameter w...
متن کاملEffect of Deformation Temperature on the Mechanical Behavior of a New TRIP/TWIP Steel Containing 21% Manganese
In recent years, TRIP/TWIP steels have been the focus of great attention thanks due to their excellent tensile strength-ductility combination. The compression tests were performed at different temperatures from 25 to1000°C to study the mechanical behavior of advanced austenitic steel with 21% manganese plus bearing Ti. The results indicated that the plastic deformation is controlled by deformat...
متن کاملEffect of plastic deformation on anelastic mechanical losses in multicomponent substitutional austenitic alloys
Complex two-component peak of anelastic mechanical losses was observed in multicomponent substitutional austenitic alloys after prior plastic deformation. In AISI 316L, AISI 316LN, AISI 310 and AISI 304 austenitic stainless steels, this peak is situated in the wide range of temperature from 200 to 400K. Characteristics of the observed peak for different thermo-mechanical treatments were studied...