Effect of superimposed uniaxial stress on rumpling of platinum-modified nickel aluminide coatings
نویسندگان
چکیده
Thermal cycling of a platinum modified, nickel aluminide (Ni,Pt)Al coated single crystal superalloy, between 1000 and 1150 C with 10 min holds at each temperature, and subject to a compressive uniaxial stress is reported. There are two major effects of the superimposed compressive stress not observed in the absence of the stress. One is that the rumpling pattern exhibits an asymmetry with an increase of the bond coat surface roughness perpendicular to the applied loading axis. The other is the formation of cracks in the thermally grown oxide aligned parallel to the stress axis. 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
منابع مشابه
On the initiation of cyclic oxidation-induced rumpling of platinum-modified nickel aluminide coatings
The evolution of the surface roughness of an initially flat platinum-modified nickel aluminide (NiPtAl) coating on a single crystal superalloy with cyclic oxidation has been measured by optical profilometry and correlated with the aluminide microstructure. The roughness evolution is dominated by the relative motion of individual grains on thermal cycling, with the larger sized grains moving up ...
متن کاملNickel Base Superalloy Rene®80 – The Effect of High Temperature Cyclic Oxidation on Platinum-Aluminide Coating Features
Nickel base superalloy alloys are used in the manufacture of gas turbine engine components, which in use are exposed to high temperatures and corrosive environments. The platinum aluminide coatings described here have been developed to protect nickel base superalloy alloys from oxidation. In this study, the effect of cyclic oxidation, platinum layer thickness and aluminizing process on beha...
متن کاملCyclic oxidation-induced cracking of platinum-modified nickel-aluminide coatings
Short cracks, extending to the interdiffusion zone, have been observed in platinum-modified nickel-aluminide diffusion coatings on single-crystal CMSX-4 superalloys after these have been subject to short (10 min) rapid thermal cycles. The cracks were revealed after removing the thermally grown oxide formed during cycling on the coating surfaces. Cracking was observed for coatings subject to the...
متن کاملFormation and Evaluation of Oxidation Behavior of Zirconia- Aluminide Coating on Nickel- Based Alloy
Practical applications of thermal barrier coatings with aluminide bond-coats are limited due to oxide scale spallation of the aluminide coating under applied thermal stresses. Considering the positive effects of oxygen-active elements or their oxides on the high temperature oxidation behavior, in this research zirconia was introduced into an aluminide coating. For this purpose, a Watts type bat...
متن کاملThe Effect of Platinum Layer and Aluminizing Process on Surface Roughness of Coated Superalloy by Pt-Al
In this study, the effect of platinum-aluminide coating parameters on surface roughness of nickel-based superalloy Rene®80 was evaluated. For this purpose, different thicknesses of Pt-layer (2, 4, 6 and 8µm) were plated on the Samples. Then diffusion aluminide coating in two types, high tempeature-low activity and low temperature-high activity was performed. The results of structural investigat...
متن کامل