Grain rotations in ultrafine-grained aluminum films studied using in situ TEM straining with automated crystal orientation mapping
نویسندگان
چکیده
• Large grain rotations occur during loading and are partially or fully reversible in a significant fraction of grains during
منابع مشابه
Texture dependent strain rate sensitivity of ultrafine-grained aluminum films
Article history: Received 25 October 2015 Received in revised form 2 December 2015 Accepted 3 December 2015 Available online 17 December 2015 We investigated the strain rate sensitivity (SRS) of freestanding ultrafine-grained aluminum films with similar thickness (~240 nm) and mean grain size (~275 nm) but highly dissimilar texture. For (110) textured bicrystalline films, flow stress increased ...
متن کاملDeformation-induced grain growth and twinning in nanocrystalline palladium thin films
The microstructure and mechanical properties of nanocrystalline Pd films prepared by magnetron sputtering have been investigated as a function of strain. The films were deposited onto polyimide substrates and tested in tensile mode. In order to follow the deformation processes in the material, several samples were strained to defined straining states, up to a maximum engineering strain of 10%, ...
متن کاملIn situ observation of deformation processes in nanocrystalline face-centered cubic metals
The atomistic mechanisms active during plastic deformation of nanocrystalline metals are still a subject of controversy. The recently developed approach of combining automated crystal orientation mapping (ACOM) and in situ straining inside a transmission electron microscope was applied to study the deformation of nanocrystalline Pd x Au1- x thin films. This combination enables direct imaging of...
متن کاملRecrystallization texture during ECAP processing of ultrafine/nano grained magnesium alloy
An ultrafine/nano grained AZ31 magnesium alloy was produced through four-pass ECAP processing. TEM microscopy indicated that recrystallized regions included nano grains of 75 nm. Pole figures showed that a fiber basal texture with two-pole peaks was developed after four passes, where a basal pole peak lies parallel to the extrusion direction (ED) and the other ~20° away from the transverse dire...
متن کاملDynamic observations of deformation in an ultrafine-grained Al–Mg alloy with bimodal grain structure
The tensile properties and deformation response of an ultrafine-grained (UFG) Al–Mg alloy with bimodal grain structure were investigated using a micro-straining unit and a strain mapping technique. Atomized Al 5083 powder was ball-milled in liquid N2 to obtain a nanocrystalline (NC) structure, then blended with 50 wt.% unmilled coarse-grained (CG) powder, and consolidated to produce a bimodal g...
متن کامل