Precipitation in Fe- or Ni-implanted and annealed GaAs
نویسندگان
چکیده
We report the formation of metal/semiconductor composites by ion implantation of Fe and Ni into GaAs and a subsequent anneal to nucleate clusters. Electron diffraction experiments and high resolution transmission electron microscopy images indicate that these precipitates are probably hexagonal and metallic Fe3GaAs or Ni3GaAs with orientation relationship to GaAs of ~101̄0!ppi~422̄!m , ~0002!ppi~111̄!m , and @12̄10#ppi@011#m . Correlation of the electrical and structural properties of the samples annealed at different temperatures shows that the buried Schottky-barrier model has general applicability. © 1994 American Institute of Physics.
منابع مشابه
Structure and Magnetic Properties of Oxide Nanoparticles of Fe-Co-Ni Synthesized by Co-Precipitation Method
Oxide nanoparticles of Fe-Co-Ni were prepared in six different compositions by co-precipitation method. The as-synthesized nanoparticles were characterized by X-Ray Diffraction (XRD), Field Emission Scanning Electron microscope (FESEM), Fourier Transform Infrared (FT-IR) and Vibrating Sample Magnetometer (VSM). It was found that the nanoparticles had mean crystalline size of 30-55 nm and spher...
متن کاملPositive and Negative Temperature Dependence in the Resistivity of Crystallized Zr-Fe-Ni Metallic Glasses
Ni0.25Fe0.75Zr₃ metallic glassy ribbons were annealed in evacuated quartz ampoules beyond the crystallization temperatures (Tx ~655 K) over the range 773 to 1,173 K for varying periods of time. The resistivity of samples annealed over the temperature range 923 to 1,073 K for periods less than four hours increased as a function of decreasing temperature, while it decreased for samples annealed f...
متن کاملPhotoluminescence and damage recovery studies in Fe-implanted ZnO single crystals
We report Fe-related emission in ion-implanted ZnO single crystals. Iron ions were implanted at room temperature with 100 keV and a fluence of 1310 Fe/cm, and were submitted to annealing treatments in vacuum and in air. After implantation, the damage raises the minimum yield (xmin) from 2% to 50%. Annealing in an oxidizing atmosphere leads to a reduction of the implantation damage, which is ful...
متن کاملThe Effect of Nickel Increasing and Aluminum Addition on Sulfidation Resistance of Fe-Ni-Cr Alloys (TECHNICAL NOTE)
In this research the effects of; increasing the amount of nickel and adding aluminum to create and prolong sulfidation resistance of Fe-Ni-Cr alloys have been investigated. Sulfidation tests were carried out at 1100°C in S/O bearing atmosphere. Prior to the tests, the specimens were annealed in argon at 1250°C for 8 hrs. Weight changes were measured and corroded deposits were analyzed byscannin...