Symmetry-Related Transitions in the Spectrum of Nanosized Cubic Y2O3:Tb3+

Herein the preparation and cathodoluminescence of nanoparticles of cubic Y2O3:Tb3+ having Tb3+ concentration varying between 0.1 and 10 Mol% are described. The cathodoluminescence spectra were recorded with a high resolution spectrometer, which enabled the identification of Tb3+ lines with C2 and S6 symmetry: the lines at 542.8 nm and 544.4 nm were designated as D4→F5 (C2) and D4→F5 (S6) respectively. The critical distance for energy transfer from Tb3+ ions at S6 lattice sites to Tb3+ ions at C2 lattice sites was found to be >1.7 nm. At the greater distances which prevail at low Tb3+ concentration, this energy transfer virtually stops. From cathodoluminescence spectra recorded in a scanning transmission electron microscope it was concluded that this energy transfer also did not take place if the temperature was reduced below 102 K. The efficiency of the cathodoluminescence of 1% Y2O3:Tb3+ was 6 lm/w at a beam voltage of 15 kV. The decay time of the D4→F5 (C2) transition was substantially shorter than that of the D4→F5 (S6) transition at low Tb3+ concentrations. The decay behavior of the cathodoluminescence images in a field emission scanning electron microscope has been explained in terms of phosphor saturation. © The Author(s) 2015. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution 4.0 License (CC BY, http://creativecommons.org/licenses/by/4.0/), which permits unrestricted reuse of the work in any medium, provided the original work is properly cited. [DOI: 10.1149/2.0251507jss] All rights reserved.