Objective Mineral trioxide aggregate (MTA) cements contain two types of particles, namely Portland cement (PC) (nominally 80% w/w) and bismuth oxide (BO) (20%). This study aims to determine the particle size distribution (PSD) of PC and BO found in MTA. Materials and methods The PSDs of ProRoot MTA (MTA-P) and MTA Angelus (MTA-A) powder were determined using laser diffraction, and compared to samples of PC (at three different particle sizes) and BO. The non-linear least squares method was used to deconvolute the PSDs into the constituents. MTA-P and MTA-A powders were also assessed with scanning electron microscopy. Results BO showed a near Gaussian distribution for particle size, with a mode distribution peak at 10.48 μm. PC samples milled to differing degrees of fineness had mode distribution peaks from 19.31 down to 4.88 μm. MTA-P had a complex PSD composed of both fine and large PC particles, with BO at an intermediate size, whereas MTA-A had only small BO particles and large PC particles. Conclusions The PSD of MTA cement products is bimodal or more complex, which has implications for understanding how particle size influences the overall properties of the material. Smaller particles may be reactive PC or unreactive radiopaque agent. Manufacturers should disclose particle size information for PC and radiopaque agents to prevent simplistic conclusions being drawn from statements of average particle size for MTA materials.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Assessment of antifungal activity of Proroot mineral trioxide aggregate and mineral trioxide aggregate-Angelus

BACKGROUND Fungi may play a key part in periradicular diseases. The aim of this study was to evaluate and compare the antifungal properties of two root-end filling materials, ProRoot Mineral trioxide aggregate (MTA) and MTA-Angelus, against Candida albicans using tube-dilution test. MATERIALS AND METHODS The antifungal properties of ProRoot MTA and MTA-Angelus against C. albicans was assessed...

متن کامل

The effect of various mixing techniques on the surface microhardness of mineral trioxide aggregate.

AIM To evaluate the influence of various mixing procedures including ultrasonic vibration, trituration of customized encapsulated mineral trioxide aggregate (MTA) and condensation on the Vickers surface microhardness of MTA. METHODOLOGY ProRoot MTA Original, ProRoot MTA (white), MTA-Angelus (grey) and MTA White Angelus (white) were prepared using several mixing techniques including ultrasonic...

متن کامل

Cytotoxicity of newly developed pozzolan cement and other root-end filling materials on human periodontal ligament cell

OBJECTIVES The purpose of this study was to evaluate in vitro cytotoxicity of the pozzolan cement and other root-end filling materials using human periodontal ligament cell. MATERIALS AND METHODS Endocem (Maruchi), white ProRoot MTA (Dentsply), white Angelus MTA (Angelus), and Super EBA (Bosworth Co.) were tested after set completely in an incubator at 37℃ for 7 days, Endocem was tested in tw...

متن کامل

Sealing ability of MTA and radiopaque Portland cement with or without calcium chloride for root-end filling.

The aim of this study was to evaluate the influence of calcium chloride (CaCl(2)) on the sealing ability of three Mineral Trioxide Aggregate (MTA) cements, ProRoot MTA, MTA-Angelus, and radiopaque White Portland cement (WPC), for retrograde root filling. Seventy roots of extracted single-rooted teeth were instrumented and obturated. After sectioning the samples at 2 mm from the apex, they recei...

متن کامل

In vitro evaluation of the cytotoxicity of ProRoot MTA and MTA Angelus.

The purpose of the present in vitro study was to compare the cytotoxic effect of two commercially available brands of mineral trioxide cement (ProRoot MTA and MTA Angelus), modified zinc oxide-eugenol cement (SuperEBA) and resin-modified glass ionomer cement (Vitrebond) using rat pulp cells (RPC-C2A) and human lung fibroblasts (MRC-5). The cells were cultured in typical culture conditions and e...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 2  شماره 

صفحات  -

تاریخ انتشار 2016