Preparation of Concrete Superplasticizer by Oxidation- Sulfomethylation of Sodium Lignosulfonate
نویسندگان
چکیده
Modification of sodium lignosulfonate (SLS) via combined oxidationsulfomethylation was employed to prepare concrete superplasticizer. It was found that the oxidation of SLS by peroxyacetic acid facilitated the subsequent sulfomethylation. After modification, both the molecular weight and sulfo group content were significantly increased, and thus the performance of SLS as water reducer was improved. With the water to cement ratio at 0.4 and 0.3% (w/w) modified SLS, the fluidity of cement paste could reach 185 mm, which was 15% higher than that with unmodified SLS. It was also comparable to the performance of commercial naphthalene superplasticizer under the same conditions.
منابع مشابه
Oxidation and Sulfomethylation of Alkali- Extracted Lignin from Corn Stalk
A lignosulfonate was prepared from alkali-extracted corn stalk lignin (AEL) by oxidation under mild conditions and sulfomethylation. The oxidized AEL exhibited lower molecular weight, narrower molecular weight distribution, and higher phenolic hydroxyl content than AEL, demonstrating that oxidized AEL was more reactive than those before oxidation. The content of sulfonic groups was significantl...
متن کاملAlkali-O2 oxidized lignin – A bio-based concrete plasticizer
Commercial wheat straw soda lignin was used to develop an alkali-O2 oxidation method to produce a ready-to-use solution for concrete plasticizing (cement dispersing). Lignin characterization was done directly from the solution. Depending on conditions, oxidation primarily induced either condensation or degradation of lignin. Thus, both the negative charge and the molar mass of the lignin were c...
متن کاملEffect of Superplasticizer and NaOH Molarity on Workability, Compressive Strength and Microstructure Properties of Self-Compacting Geopolymer Concrete
The research investigates the effects of super plasticizer and molarity of sodium hydroxide alkaline solution on the workability, microstructure and compressive strength of self compacting geopolymer concrete (SCGC). SCGC is an improved way of concreting execution that does not require compaction and is made by complete elimination of ordinary Portland cement content. The parameters studied wer...
متن کاملCoproduction of ethanol and lignosulfonate from Moso bamboo residues
In the course of utilization of moso bamboo, some fractions are not effectively utilized due to the weakness in mechanical properties. Only a part of these residues are recovered for energy production or made into activated carbon; the remainder are discarded resulting in environment pollution (Mui et al., 2008). As the bamboo residue is a kind of polysaccharides-rich lignocellulosic material, ...
متن کاملPreparation ZrO2 ceramic coating by electrolytic plasma oxidation and study of the effect of monoclinic/tetragonal phases on the corrosion resistance of the coating
In this paper, zirconium oxide ceramics coating (ZrO2) were produced on Zircaloy-4 alloy using plasma electrolytic oxidation (PEO). Sodium silicate and Sodium aluminate based electrolyte was selected in PEO process and the effects of the concentration of Sodium aluminate (0, 2.5, 5, 7.5, and 10 g/L) on the microstructure, phase structure and the behavior of corrosion of formed coatings. In orde...
متن کامل