Cation distribution and vacancies in nickel cobaltite.

نویسندگان

  • Danilo Loche
  • Claudia Marras
  • Daniela Carta
  • Maria Francesca Casula
  • Gavin Mountjoy
  • Anna Corrias
چکیده

Samples of nickel cobaltite, a mixed oxide occurring in the spinel structure which is currently extensively investigated because of its prospective application as ferromagnetic, electrocatalytic, and cost-effective energy storage material were prepared in the form of nanocrystals stabilized in a highly porous silica aerogel and as unsupported nanoparticles. Nickel cobaltite nanocrystals with average size 4 nm are successfully grown for the first time into the silica aerogel provided that a controlled oxidation of the metal precursor phases is carried out, consisting in a reduction under H2 flow followed by mild oxidation in air. The investigation of the average oxidation state of the cations and of their distribution between the sites within the spinel structure, which is commonly described assuming the Ni cations are only located in the octahedral sites, has been carried out by X-ray absorption spectroscopy providing evidence for the first time that the unsupported nickel cobaltite sample has a Ni : Co molar ratio higher than the nominal ratio of 1 : 2 and a larger than expected average overall oxidation state of the cobalt and nickel cations. This is achieved retaining the spinel structure, which accommodates vacancies to counterbalance the variation in oxidation state.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

DISORDER IN LAYERED HYDROXIDES: DIFFaX SIMULATION OF THE X-RAY POWDER DIFFRACTION PATTERNS OF NICKEL HYDROXIDE

Layered metal hydroxides exhibit non-uniform broadening of lines in their X-ray powder diffraction (XRPD) patterns, which cannot always be explained on the basis of crystallite size effects. In the case of hexagonal solids such as nickel hydroxide, DIFFaX simulations of the XRPD patterns show that: (1) stacking faults and turbostratic disorder at low (<30%) incidence selectively broaden the h0l...

متن کامل

Fabrication and Electrochemical Characterization of Polyvinyl Chloride Based/Chitosan-co- Iron Nickel Oxide Nanoparticles Composite Heterogeneous Cation Exchange Membranes

In this research, polyvinylchloride based composite heterogeneous cation exchange membranes were prepared by the solution casting technique. Chitosan-co-iron nickel oxide nanoparticles were utilized as membrane surface modifier to improve the membranes electrochemical properties. The effect of additive nanoparticle concentration in the modifier solution on the properties of composite membranes ...

متن کامل

The Effect of Nano-Additives on the Hydration Resistance of Materials Synthesized From the MgO-CaO System (RESEARCH NOTE)

In this study, the effect of variety of Nano- additives doping on the hydration resistance of the MgO-CaO system was investigated. Samples were prepared from calcined dolomite and magnesite. Nano-additives that contained cations with various valences (trivalent and tetravalent) used as  a dopant. The bulk density, apparent porosity and hydration resitance were studied and evaluated. Also, phase...

متن کامل

Analysis of the NiCo2O4 spinel surface with Auger and X-ray photoelectron spectroscopy

Nickel cobaltite, NiCo2O4, has been synthesized by sol–gel and thermal decomposition techniques and the surface composition studied with Auger (AES) and X-ray photoelectron spectroscopies (XPS). The asintroduced samples are near-stoichiometric, although samples fabricated by thermal decomposition tend to be oxygen-defi cient by approximately 25% of the predicted spinel concentration. Nickel 2p ...

متن کامل

Enhanced Oxidation of Nickel at Room Temperature by Low-energy Oxygen Implantation

The formation of oxide films on pure Ni surfaces by low energy oxygen ion-beam bombardment at room temperature was studied by X-ray photoelectron spectroscopy. Ion-induced oxidation is more efficient in creating thin NiO films on Ni surfaces than oxidation in oxygen atmosphere. The oxide thickness of bombarded samples is related to the penetration depth of oxygen ions in Ni and scales with the ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Physical chemistry chemical physics : PCCP

دوره 19 25  شماره 

صفحات  -

تاریخ انتشار 2017