The solubility of four dental cement bases was measured in simulated dentinal fluid and distilled water to evaluate the relevancy of the American Dental Association solubility test for cement bases in contact with vital dentine. A simulated dentinal fluid was formulated utilizing glucose, distilled water, and sterile human plasma. Cement-base samples were immersed in either distilled water or simulated dentinal fluid at 37 degrees C in a shaker water-bath for 1, 2, or 3 months. Weight loss values were compared utilizing a three-way analysis of variance. Zinc oxide-eugenol cements were significantly more soluble in simulated dentinal fluid than distilled water, while the calcium hydroxide cement bases were significantly more soluble in distilled water than simulated dentinal fluid.
منابع مشابه
بررسی خواص فیزیکی و قابلیت انحلال و تجزیه پذیری سیمانهای حاوی عنصر روی در دندانپزشکی ترمیمی و مقایسه آنها با مقادیر استاندارد
Statement of Problem: Zinc contained cements are so important among dental material as they have many indications and used in different ways therefore evaluation of their physical properties is so important in dentistry.Purpose: The purpose of this research was to measure some physical properties of zinc-contained cements used in restorative dentistry. These cements included: Zinc oxide-eugenol...
متن کاملEvaluation of the Radiopacity of Some Luting, Lining and Filling Dental Cements
Background and Aim: To investigate the radiopacity of different luting, lining and filling dental cements used in prosthetic dentistry in comparison with human and bovine dental hard tissues. Material and methods: Eight cylindrical samples of each material (6 x 1 mm) were prepared from Aqualox (APC), Durelon (DE) and Adhesor Carbofine (ACF) zinc polycarboxylate cements, Cavex zinc oxide eugenol...
متن کاملWater Sorption and Solubility of Provisional and Permanent Luting Cements Geçici ve Daimi Yapıştırma Simanlarının Su Absorbsiyonu ve Çözünürlükleri
Results: All materials tested demonstrated different degrees of sorption and solubility. The glass ionomer cement had the best value for sorption. The zinc oxide eugenol and eugenol free cements had lower water sorption than the zinc polycarboxylate and zinc phosphate cements were evaluated. Some materials retained water in their structure and thus compensated for any loss of mass due to dissol...
متن کاملInfluence of provisional cements on ultimate bond strength of indirect composite restorations to dentin.
PURPOSE The aim of this study was to evaluate the effect of provisional cements on the adhesion of resin bonded indirect restorations and determine the best method for avoiding adverse effects. MATERIALS AND METHODS Forty-five bovine incisors were selected, and the enamel removed with a 600-grit SiC abrasive disk to expose superficial dentin. Provisional restorations of acrylic resin were cem...
متن کاملA study on the sealing ability and antibacterial activity of Ca3SiO5/CaCl2 composite cement for dental applications.
The objective of this study was to evaluate the sealing ability and antibacterial activity of Ca3SiO5/CaCl2 composite cement. Fifty maxillary anterior teeth were instrumented according to step-back technique and filled with experimental and control materials. To evaluate the sealing ability, a fluid transport model using glucose was employed for quantitative analysis of endodontic microleakage....
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Journal of oral rehabilitation
دوره 16 5 شماره
صفحات -
تاریخ انتشار 1989