The effect of Ti and O ion implantation on the resistive switching in Pt/TiO2-x/Pt devices
نویسندگان
چکیده
The effects of Ti and O implantation on TiO2-x resistive switches are systemically investigated. The forming voltage drops monotonically with Ti implantation dose and forming vanishes completely at 10 ions/cm, whereas oxygen implantation causes a decrease and then increase in forming voltage. The ON/OFF current ratio becomes worse with high Ti implantation due to increased leakage currents through the TiO2 film. Furthermore, the forming voltage minimum induced by oxygen implantation can be shifted by thermal annealing, suggesting a careful balance between oxidation, reduction, and ion implantation
منابع مشابه
Investigation of resistive switching in anodized titanium dioxide thin films
In this work, TiO2 nanostructures were grown on titanium thin films by electrochemical anodizing method. The bipolar resistive switching effect has been observed in Pt/TiO2/Ti device. Resistive switching characteristics indicated the TiO2 nanotubes are one of the potential materials for nonvolatile memory applications. Increasing anodizing duration will increase nanotube lengths which itself c...
متن کاملBipolar Resistive Switching Characteristics of HfO2/TiO2/HfO2 Trilayer-Structure RRAM Devices on Pt and TiN-Coated Substrates Fabricated by Atomic Layer Deposition
The HfO2/TiO2/HfO2 trilayer-structure resistive random access memory (RRAM) devices have been fabricated on Pt- and TiN-coated Si substrates with Pt top electrodes by atomic layer deposition (ALD). The effect of the bottom electrodes of Pt and TiN on the resistive switching properties of trilayer-structure units has been investigated. Both Pt/HfO2/TiO2/HfO2/Pt and Pt/HfO2/TiO2/HfO2/TiN exhibit ...
متن کاملKey concepts behind forming-free resistive switching incorporated with rectifying transport properties
This work reports the effect of Ti diffusion on the bipolar resistive switching in Au/BiFeO3/Pt/Ti capacitor-like structures. Polycrystalline BiFeO3 thin films are deposited by pulsed laser deposition at different temperatures on Pt/Ti/SiO2/Si substrates. From the energy filtered transmission electron microscopy and Rutherford backscattering spectrometry it is observed that Ti diffusion occurs ...
متن کاملDesign of Highly Uniform Platinum and Palladium Nanoparticle Decoration on TiO2 Nanotube Arrays: An Efficient Anode to the Electro-Oxidation of Alcohols
We explore electro-catalytic properties of a system consisting of platinum and palladium nanoparticles dispersed over a nanotubular self-organized TiO2 matrix. These electrodes prepared by electroess and microemulsion of palladium and palladium nanoparticles on to TiO2 nanotubes, respectively. Titanium oxide nanotubes were fabricated by anodizing titanium foil in ethylene glycol (EG) fluoride-c...
متن کاملTailoring resistive switching in Pt/SrTiO3 junctions by stoichiometry control
Resistive switching effects in transition metal oxide-based devices offer new opportunities for information storage and computing technologies. Although it is known that resistive switching is a defect-driven phenomenon, the precise mechanisms are still poorly understood owing to the difficulty of systematically controlling specific point defects. As a result, obtaining reliable and reproducibl...
متن کامل