Effect of SO2 and steam on CO2 capture performance of biomass-templated calcium aluminate pellets.
نویسندگان
چکیده
Four types of synthetic sorbents were developed for high-temperature post-combustion calcium looping CO2 capture using Longcal limestone. Pellets were prepared with: lime and cement (LC); lime and flour (LF); lime, cement and flour (LCF); and lime, cement and flour doped with seawater (LCFSW). Flour was used as a templating material. All samples underwent 20 cycles in a TGA under two different calcination conditions. Moreover, the prepared sorbents were tested for 10 carbonation/calcination cycles in a 68 mm-internal-diameter bubbling fluidized bed (BFB) in three environments: with no sulphur and no steam; in the presence of sulphur; and with steam. When compared to limestone, all the synthetic sorbents exhibited enhanced CO2 capture performance in the BFB experiments, with the exception of the sample doped with seawater. In the BFB tests, the addition of cement binder during the pelletisation process resulted in the increase of CO2 capture capacity from 0.08 g CO2 per g sorbent (LF) to 0.15 g CO2 per g sorbent (LCF) by the 10th cycle. The CO2 uptake in the presence of SO2 dramatically declined by the 10th cycle; for example, from 0.22 g CO2 per g sorbent to 0.05 g CO2 per g sorbent in the case of the untemplated material (LC). However, as expected all samples showed improved performance in the presence of steam, and the decay of reactivity during the cycles was less pronounced. Nevertheless, in the BFB environment, the templated pellets showed poorer CO2 capture performance. This is presumably because of material loss due to attrition under the FB conditions. By contrast, the templated materials performed better than untemplated materials under TGA conditions. This indicates that the reduction of attrition is critical when employing templated materials in realistic systems with FB reactors.
منابع مشابه
CO2 Capture Performance Using Biomass-templated Cement-supported Limestone Pellets
Synthetic biomass-templated cement-supported CaO-based sorbents were produced by granulation process for high-temperature post-combustion CO2 capture. Commercial flour was used as the biomass and served as a templating agent. The investigation of porosity showed that the pellets with biomass or cement resulted in enhancement of porosity. Four types of sorbents containing varying proportions of ...
متن کاملA combined catalyst and sorbent for enhancing hydrogen production from coal or biomass
Future large-scale production of H2 for use as a clean fuel will likely depend upon gasifying coal or biomass followed by steam reforming the resulting gas mixture and separating the CO2 byproduct. The process of steam reforming and CO2 separation can be greatly simplified by utilizing a new material that combines a reforming catalyst with a sorbent for CO2. Such a material was prepared in the ...
متن کاملCatalytic Effect of Metal Species on Enhancement of CO2 Gasification Reactivity of Biomass Char
In the Boudouard reaction, where CO2 is reacted with carbon (char) to produce CO, very high temperatures are required to shift the equilibrium towards CO production. This endothermic reaction is inherently slow and catalytic species are effective to speed up the reaction rate at temperatures below 900 °C. In this study, the catalytic effect of some alkali (K, Na), alkaline earth (Ca) and transi...
متن کاملBiomass Steam Gasification with In-Situ CO2 Capture for Enriched Hydrogen Gas Production: A Reaction Kinetics Modelling Approach
Due to energy and environmental issues, hydrogen has become a more attractive clean fuel. Furthermore, there is high interest in producing hydrogen from biomass with a view to sustainability. The thermochemical process for hydrogen production, i.e. gasification, is the focus of this work. This paper discusses the mathematical modeling of hydrogen production process via biomass steam gasificatio...
متن کاملDevelopment of New Potassium Carbonate Sorbent for CO2 Capture under Real Flue Gas Conditions
In this paper, the development of a new potassium carbonateon alumina support sorbent prepared by impregnating K2CO3 with an industrial grade of Al2O3 support was investigated. The CO2 capture capacity was measured using real flue gas with 8% CO2 and 12% H2O in a fixed-bed reactor at a temperature of 65 °C using breakthrough curves. The developed sorbent showed an adsorption capacity of 66.2 mg...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Faraday discussions
دوره 192 شماره
صفحات -
تاریخ انتشار 2016